Abstract:Bimetallic CoCu model catalysts were investigated for the synthesis of higher alcohols using catalytic CO hydrogenation according to the Fischer–Tropsch technology. Emphasis was placed on revealing the influence of the activation conditions. Accordingly, catalyst precursors were activated in argon, hydrogen, syngas (CO/H2), and CO under atmospheric conditions and at elevated temperatures (370 °C). All catalyst precursors were prepared via oxalate coprecipitation in the absence of a classic support. Alcohol selectivities between 30 and ∼40% (up to ∼50% for the sum of alcohols and alkenes) were obtained with an Anderson–Schulz–Flory (ASF) chain lengthening probability maximizing the slate up to C6. Detailed catalysis and characterization studies were performed using a Co2Cu1 catalyst composition. The catalytic performances of the H2- and syngas-activated Co2Cu1 catalyst were similar. While the CO-activated catalyst shows significantly higher catalytic activity and ASF chain lengthening probability, the alcohol selectivities are lower than those of H2- or syngas-activated ones. All catalysts required time on stream for several hours to achieve steady-state catalytic performance. Co2Cu1 catalysts were characterized by temperature-programmed decomposition (TPDec), in situ N2 physisorption (Brunauer–Emmett–Teller), transmission electron microscopy (TEM), and in situ X-ray photoelectron spectroscopy (XPS). The data indicate major restructuring occurs during activation. An “onion-like” graphitic carbon shell was observed via TEM for the CO-activated Co2Cu1 catalyst, which probably originated mainly from the Boudouard reaction (2CO + [ ]ad → Cad + CO2). This interpretation is in accordance with the TPDec profiles and XPS results. The latter also indicates that syngas and CO activation lead to higher than nominal Co/Cu surface ratios. The surface segregation of Co in the presence of CO atmospheres is interpreted on the basis of Co@Cu core–shell structured particles.

CO hydrogenation to higher alcohols over CuZnAl catalysts without promoters: Effect of pH value in catalyst preparation

Effects of CuO/ZnO Ratio and Preparation Conditions on Performance of CuO-ZnO Catalysts in Preparing C4～C6 Polyols through Sorbitol Hydrogenolysis

Higher alcohols synthesis from syngas over P-promoted non-noble metal Cu-based catalyst

Insight into the structural sensitivity of CuZnAl catalysts for CO hydrogenation to alcohols

CuZnAl@S-1 Catalyst for the Synthesis of Higher Alcohols by CO Hydrogenation

Effect of CaO Modification on Performance of CuZnAlZr Catalyst in Synthesis of Higher Alcohols from Synthesis Gas

Hydrothermal synthesis of ZnZrO x catalysts for CO2 hydrogenation to methanol: the effect of pH on structure and activity

Higher Alcohols through CO Hydrogenation over CoCu Catalysts: Influence of Precursor Activation

Roles Investigation of Promoters in K/Cu–Zn Catalyst and Higher Alcohols Synthesis from CO2 Hydrogenation over a Novel Two-Stage Bed Catalyst Combination System

Tuning CuO crystallite size by different solvents for higher alcohols synthesis from syngas over CuZnAl catalyst

The effect of CuO crystallite size on the structure and performance of CuZnAl catalyst for mixed alcohols synthesis from syngas

Higher Alcohols Synthesis from Syngas over Cocu/Sio2 Catalysts: Dynamic Structure and the Role of Cu

Synthesis of mixed higher alcohols over Fe promoted Cu/ZrO2 catalysts by CO hydrogenation

The Support Effects on the Direct Conversion of Syngas to Higher Alcohol Synthesis over Copper-Based Catalysts

Synergy between Active Sites of Ternary CuZnAlOOH Catalysts in CO Hydrogenation to Ethanol and Higher Alcohols

Impact of Cu complex anions on CuZnAl intercalated hydrotalcite-like catalysts for low-carbon alcohols synthesis from syngas

Preparation of Cu/ZnO/Al2O3 Catalysts in a Solvent-Free Routine for CO Hydrogenation

Synthesis Of Higher Alcohol Mixtures From Syngas Over Modified Copper Catalysts