Abstract:Two types of amorphous ZrO2 (am-ZrO2) catalysts were prepared by different co-precipitation/reflux digestion methods (with ethylenediamine and ammonia as the precipitant respectively). Then, copper and potassium were introduced for modifying ZrO2 via an impregnation method to enhance the catalytic performance. The obtained catalysts were further characterized by means of Brunauer-Emmett-Teller surface areas (BET), X-ray diffraction (XRD), H2-temperature-programmed reduction (H2-TPR), and In situ diffuse reflectance infrared spectroscopy (in situ DRIFTS). CO hydrogenation experiments were performed in a fixed-bed reactor for isobutanol synthesis. Great differences were observed on the distribution of alcohols over the two types of ZrO2 catalysts, which were promoted with the same content of Cu and K. The selectivity of isobutanol on K-CuZrO2 (ammonia as precipitant, A-KCZ) was three times higher than that on K-CuZrO2 (ethylenediamine as precipitant, E-KCZ). The characterization results indicated that the A-KCZ catalyst supplied more active hydroxyls (isolated hydroxyls) for anchoring and dispersing Cu. More importantly, it was found that bicarbonate species were formed, which were ascribed as important C1 species for isobutanol formation on the A-KCZ catalyst surface. These C1 intermediates had relatively stronger adsorption strength than those adsorbed on the E-KCZ catalyst, indicating that the bicarbonate species on the A-KCZ catalyst had a longer residence time for further carbon chain growth. Therefore, the selectivity of isobutanol was greatly enhanced. These findings would extend the horizontal of direct alcohols synthesis from syngas.

Effect of CaO Modification on Performance of CuZnAlZr Catalyst in Synthesis of Higher Alcohols from Synthesis Gas

Synthesis Of Higher Alcohol Mixtures From Syngas Over Modified Copper Catalysts

The effect of CuO crystallite size on the structure and performance of CuZnAl catalyst for mixed alcohols synthesis from syngas

Influences of preparation methods of ZrO2 support and treatment conditions of Cu/ZrO2 catalysts on synthesis of methanol via CO hydrogenation

CuZnAl@S-1 Catalyst for the Synthesis of Higher Alcohols by CO Hydrogenation

Oxygen Vacancy Control of Catalytic Activity of Cu/ZnO for Higher Alcohols Synthesis via Incorporating Ga

Effect of La modified Cu/ZrO2 catalysts on alcohol synthesis

Impact of Cu complex anions on CuZnAl intercalated hydrotalcite-like catalysts for low-carbon alcohols synthesis from syngas

Enhanced selectivity to methanol in CO2 hydrogenation on CuO/ZrO2 catalysts by alkali metal modification

Modulation of Al2O3 and ZrO2 composite in Cu/ZnO-based catalysts with enhanced performance for CO2 hydrogenation to methanol

Synthesis of mixed higher alcohols over Fe promoted Cu/ZrO2 catalysts by CO hydrogenation

The Support Effects on the Direct Conversion of Syngas to Higher Alcohol Synthesis over Copper-Based Catalysts

Electronic control of catalytic activity of ZnO for higher alcohols synthesis via tailoring Fermi level

Effect of Preparation Method on ZrO2-Based Catalysts Performance for Isobutanol Synthesis from Syngas

Roles Investigation of Promoters in K/Cu–Zn Catalyst and Higher Alcohols Synthesis from CO2 Hydrogenation over a Novel Two-Stage Bed Catalyst Combination System

Tuning CuO crystallite size by different solvents for higher alcohols synthesis from syngas over CuZnAl catalyst

CO hydrogenation to higher alcohols over CuZnAl catalysts without promoters: Effect of pH value in catalyst preparation

The effect of Cu/Zn molar ratio on CO2 hydrogenation over Cu/ZnO/ZrO2/Al2O3 catalyst

Insight into the structural sensitivity of CuZnAl catalysts for CO hydrogenation to alcohols

Cu/ZnO/Al2O3 Catalyst Modulated by Zirconia with Enhanced Performance in CO2 Hydrogenation to Methanol