Abstract:Dry sliding wear tests and corresponding particulate matter (PM) analysis were conducted on a newly developed SiC-graphite-based composite friction material, paired with two types of HVOF counterface/discs: WC-CoCr and WC-FeCrAlY coatings, with a conventional martensitic stainless steel counterface as a reference. The trials were conducted on a pin-on-disc testing equipment at room temperature and a constant sliding velocity and contact pressure of 7 m/s and 0.5 MPa, respectively. The coefficient of friction (CoF) curves with the uncoated disc exhibited considerable fluctuations. On the other hand, the coated discs featured an increase in the CoF at the beginning of the tests, followed by either a continuous reduction until the end of the testing duration or the attainment of a steady state regime. The pin wear and emissions with both coatings were appreciably lower when compared to the trials with the uncoated disc. The evaluation of the friction layer observed a significant contribution of the counterface for all the pairings. The PM analysis was conducted on the particles that were lying in the range of 10 μm and 2.5 μm on a scanning electron microscope (SEM), and particles from 2.5 μm and 1 μm on transmission electron microscope (TEM), with an emphasis on the particles that were detached from the pin surface and friction layer to explain the wear mechanisms for each pairing. Through this, the need for the proper selection of both friction material and counterface to avoid the emission of harmful compounds in the environment was highlighted.

Pin-on-Disc Testing of Low-Metallic Friction Material Sliding Against HVOF Coated Cast Iron: Modelling of the Contact Temperature Evolution

Wear and Contact Temperature Evolution in Pin-on-Disc Tribotesting of Low-Metallic Friction Material Sliding Against Pearlitic Cast Iron

Sliding Behaviour of Friction Material Against Cermet Coatings: Pin-on-Disc Study of the Running-in Stage

Dry Sliding Behavior and Particulate Emissions of a SiC-graphite Composite Friction Material Paired with HVOF-Coated Counterface

The Influence of Temperature and Load on Dry Sliding Wear and Friction Property of Low Metallic Friction Material

Temperature field analysis of pin-on-disk sliding friction test

Performance of a cast-iron and WC Co-free iron-based coated disc under mild and severe brake conditions

Experimental and Modelling Study of Friction Evolution and Lubricant Breakdown Behaviour under Varying Contact Conditions in Warm Aluminium Forming Processes

Towards a better understanding of brake friction materials

Study on Simulation of Coupled Heat Transfer, Stress and Wear Behavior in Pin-on-disc Experiments

Numerical study of sliding wear caused by a loaded pin on a rotating disc

Experimental and Finite Element Analysis of Frictional Heat Distribution during Sliding Friction

Research on Sliding Wear Behavior of Co-based Alloy Based on Experiments with Material of Pin and Disc Exchanged

Modeling of contact temperatures and their influence on the tribological performance of PEEK and PTFE in a dual-pin-on-disk tribometer

Friction Reduction Due to Heating in the Sliding Contact of Smart Coating: Modeling of Mutual Effect

Dry Friction Characteristics of Ti-6Al-4V Alloy under High Sliding Velocity

Analysis of the Accuracy of Mass Difference-Based Measurement of Dry Clutch Friction Material Wear

Numerical and experimental study of the relationship between friction area and temperature of aluminium-based brake disc

The Relationships Between Tribological Behaviour and Heat-Transfer Capability of Ti6Al4V Alloys

Sliding Behavior and Particle Emissions of Cu-Free Friction Materials with Different Contents of Phenolic Resin

Influence of the Machining Process on the Wear Properties of Self-Mated Structural Steel in Dry Sliding Conditions