Abstract:Fuzz formation on a heated tungsten surface in the presence of helium-containing plasma and tungsten deposition source was investigated. Tungsten samples were exposed at 1123 K to pure helium plasma with ion incident energy of 76 eV, W/He ion flux ratio of ~0.4×10 -4 , and varied helium ion fluence from 0.18 to 3.4×10 26 m -2 . Fuzz thickness was measured by cross-sectional scanning electron microscopy to increase from 0.22 to 15 μm with increasing helium ion fluence. No indication of saturation in fuzz thickness at high fluence was observed, in contrast to fuzz produced on a tungsten surface without tungsten deposition. Additional tungsten samples were exposed at 1123 K to pure helium plasma with ion incident energy of 76 eV, helium ion fluence of ~3.4×10 26 m -2 , and varied W/He ion flux ratio from 0.26 to 3.0×10 -4 . Fuzz thickness increased from 7.5 to 120 μm with increasing W/He ratio. A final sample exposed at 1123 K to a mixed helium-deuterium plasma with ion incident energy of 76 eV, helium ion fluence of 0.18×10 26 m -2 , and W/He ion flux ratio of 2.2×10 -4 developed nearly identical fuzz structures to that developed in a pure He plasma. As a function of deposited tungsten fluence, all results were found to trace out a single layer-growth curve given by a power law relation, indicating that fuzz thickness is independent of the W/He ion flux ratio in the range investigated and independent of any deuterium present in the plasma. As a result, for tungsten plasma facing walls in magnetic fusion devices at 1000-2000 K with 10 -4 W/He ion flux ratio, fuzz with thicknesses greater than hundreds of microns may form in as little as 10 4 s (in the absence of ELM-induced erosion or annealing), and may more significantly affect its thermophysical properties than fuzz generated without a tungsten deposition source.

Observation of reduction of secondary electron emission from helium ion impact due to plasma-generated nanostructured tungsten fuzz

Secondary electron emission from plasma-generated nanostructured tungsten fuzz

Fuzz Nanostructure and Erosion on Tungsten–vanadium Alloys Exposed to Helium Plasma in the STEP Linear Plasma Device

He-ion induced surface morphology change and nanofuzz growth on hot tungsten surfaces

The dependence of tungsten fuzz layer thickness and porosity on tungsten deposition rate and helium ion fluence

Ion energy dependence of helium plasma irradiation effects on the photoelectrochemical properties of tungsten oxide

Modelling of physical sputtering properties during tungsten fuzz growth under various impact energies on NAGDIS-II

Tungsten ‘fuzz’ growth re-examined: the dependence on ion fluence in non-erosive and erosive helium plasma

Nanostructure Evolution and Surface Modification of Tungsten Exposed to Low Energy, High Flux Deuterium Plasma

Tungsten fuzz: Deposition effects and influence to fusion devices

Nanostructured fuzz growth on tungsten under low-energy and high-flux He irradiation

Helium induced nanoscopic morphology on tungsten under fusion relevant plasma conditions

A model of ballistic helium transport during helium-induced fuzz growth in tungsten

Erosion dynamics of tungsten fuzz during ELM-like heat loading

Crystal orientation effects on helium ion depth distributions and adatom formation processes in plasma-facing tungsten

Observation of Reduced-Turbulence Regime with Tungsten Injection in HL-2A Edge Plasmas

Deuterium-induced Nanostructure Formation on Tungsten Exposed to High-Flux Plasma

Initial growth of tungsten fuzz induced by bubble-driven surface stress layer under helium irradiation

Helium bubble size effects on the surface morphological response of plasma-facing tungsten

A review of late-stage tungsten fuzz growth

Formation process of tungsten nanostructure by the exposure to helium plasma under fusion relevant plasma conditions