Abstract:Highlights • Superconducting joints using carbon-doped multifilament MgB 2 wires were fabricated. • The joints showed a magnetic field screening effect up to 0.5 T at 20 K. • An SEM image of the cross-section of the joint showed a defect-free interface. • Serial sectioning revealed the formation of space or void at the interface. The development of superconducting joining technology for reacted magnesium diboride (MgB 2 ) conductors remains a critical challenge for the advancement of cryogen-free MgB 2 -based magnets for magnetic resonance imaging (MRI). Herein, the fabrication of superconducting joints using reacted carbon-doped multifilament MgB 2 wires for MRI magnets is reported. To achieve successful superconducting joints, the powder-in-mold method was employed, which involved tuning the filament protection mechanism, the powder compaction pressure, and the heat treatment condition. The fabricated joints demonstrated clear superconducting-to-normal transitions in self-field, with effective magnetic field screening up to 0.5 T at 20 K. To evaluate the interface between one of the MgB 2 filaments and the MgB 2 bulk within the joint, serial sectioning was conducted for the first time in this type of superconducting joint. The serial sectioning revealed space formation at the interface, potentially caused by the volume shrinkage associated with the MgB 2 formation or the combined effect of the volume shrinkage and the different thermal expansion coefficients of the MgB 2 bulk, the filament, the mold, and the sealing material. These findings are expected to be pivotal in developing MgB 2 superconducting joining technology for MRI magnet applications through interface engineering.

Superconducting joint of REBCO wires for MRI magnet

Development of Electromagnetic Forming Nbti Superconducting Joint

Fabrication and Test of Nb3Sn-NbTi Superconducting Joint for a 14-T MRI Magnet

Fabrication of Nbti Superconducting Joint by Electromagnetic Forming Method

Development of High Magnetic Field Magnet Technologies for the Magnetic Resonance Medical Imaging

Superconducting joints using reacted multifilament MgB 2 wires: A technology toward cryogen-free MRI magnets

Superconducting Joint and Persistent Current Switch for a 7-T Animal MRI Magnet

Development of a multi-pancake HTS magnet operated in persistent current mode based on superconducting joint of REBCO coated conductors

Development of a persistent superconducting joint between Bi-2212/Ag-alloy multifilamentary round wires

A Novel REBCO Conductor Design to Reduce Screening-Current Field in REBCO Magnets

Development of persistent joints for superconducting Bi-2212 coils

A versatile 4 K insert for characterization of the superconducting joints

Test of an 8.66-T REBCO Insert Coil with Overbanding Radial Build for a 1.3-Ghz LTS/HTS NMR Magnet

26.86-tesla direct-current magnetic field generated with an all-REBCO superconducting magnet

Progress in the Construction of a 20 T REBCO Insert Coil for High-Field All-Superconducting Magnets

Study on the Arrangement of REBCO Double-Pancake Coils with Different Critical Currents in 30-T Superconducting Magnets

Magnetization and screening current in an 800-MHz (18.8-T) REBCO NMR insert magnet: experimental results and numerical analysis

Resistance at 77K of two Bi-2223 coils with superconducting joints prepared by incongruent melting

Design of a 20 T Class REBCO Insert in a 15 T Low Temperature Superconducting Magnet

First-Cut Design of a Benchtop Cryogen-Free 23.5-T/25-mm Magnet for 1-GHz Microcoil NMR

Conceptual design of a 33 T cryogen-free magnet REBCO insert: Mechanical aspects and Protection against Thermal Runaway