Abstract:To date, the most commonly used aluminum alloys for additive manufacturing are eutectic/near-eutectic alloys. However, fabricating high strength aluminum parts has not yet been fully investigated due to solidification cracking and porosity formation, which make these alloys very hard to be processed. Electron beam selective melting (EBSM) of aluminum alloys has some advantages over selective laser melting. The process is not affected by reflectivity of aluminum powders, and parts exhibit less induced thermal stresses. In addition, oxidation is reduced due to vacuum condition. Therefore, the process provides high potential for the fabrication of aluminum alloys, specifically, Al2024 alloy which is widely used in different industries such as automotive and airline industries. Hence, these industries are highly benefitted from being able to build defect-free AM parts. This study is significant because Al2024 alloy is highly susceptible to solidification cracking and porosity formation, and crack-free samples with high relative densities have not been built by EBM process previously. The baseplate preheating temperature was set to 350 degrees C, and samples were fabricated by applying a proper powder bed preheating configuration for each layer. Different sets of processing parameters were used to investigate their effect on the performance of the parts. Archimedes technique was used to measure the relative density of samples, ranging from 95% to full-dense. The results showed that higher relative densities could be achieved by increasing the input energy to an optimum value; however, by further increasing the energy, the relative density decreases, which can be attributed to porosity formation. SEM and EBSD results showed equiaxed grains in a crack-free microstructure. Grain structure consisted of high angle grain boundaries having different crystallographic orientations with a few subgrains. Additionally, AlCuMnFe, AlCuMnFeSi, and eutectic Al2Cu phases were uniformly distributed in the alpha phase matrix. Microhardness results showed an almost uniform change of hardness values in both horizontal and vertical sections, ranging from 100 HV to 110 HV for as-built samples. Moreover, tensile and yield strengths of as-built samples reached 314 MPa and 191 MPa, respectively, which can be further increased by a proper post-processing treatment. (C) 2020 Elsevier B.V. All rights reserved.

Processing of the Heat Resistant Bearing Steel M50NiL by Selective Laser Melting

Processing of High‐Carbon Steel by Selective Electron Beam Melting

INVESTIGATION OF THE STRUCTURE AND PROPERTIES OF FERROUS NICKEL ALLOYS AFTER MOLDING BY SELECTIVE LASER MELTING

Selective laser melting of the hard-to-weld IN738LC superalloy: Efforts to mitigate defects and the resultant microstructural and mechanical properties

Additive manufacturing of Ti-45Al-4Nb-C by selective electron beam melting for automotive applications

Highly Anisotropic Steel Processed by Selective Laser Melting

Combined Thermo-Mechanical Techniques for Post-processing of the SLM-Printed Ni-Cr-Fe Alloy Parts

Selective Laser Melting Process Optimization and Mechanical Properties Evolution of AlSi10Mg by Determining Temperature of the Build Chamber using Arduino IDE and Coding Algorithm

Development of a Laser Powder Bed Fusion Process Tailored for the Additive Manufacturing of High-Quality Components Made of the Commercial Magnesium Alloy WE43

The effects of hot forging on the preform additive manufactured 316 stainless steel parts

Metal Fabrication by Additive Manufacturing Using Laser and Electron Beam Melting Technologies

Selective electron beam melting of high strength Al2024 alloy; microstructural characterization and mechanical properties

Laser Remelting Process Simulation and Optimization for Additive Manufacturing of Nickel-Based Super Alloys

Selective Laser Melting of P20 Mould Steel: Investigation on the Resultant Microstructure, High-Temperature Hardness and Corrosion Resistance

Processing AlSi10Mg by selective laser melting: parameter optimisation and material characterisation

Multimaterial Additive Manufacturing of Graded Laves Phase Reinforced NiAlTa Structures by Means of Laser Metal Deposition

A printability assessment framework for fabricating low variability nickel-niobium parts using laser powder bed fusion additive manufacturing

Effect of Heat Treatment on Microstructure and Mechanical Properties of a Selective Laser Melting Processed Ni-Based Superalloy GTD222

On the Hot Deformation Behavior of Ti-6Al-4V Made by Additive Manufacturing

Selective Laser Melting and Mechanical Properties of Stainless Steels

Selective Laser Melting of Duplex Stainless Steel 2205: Effect of Post-Processing Heat Treatment on Microstructure, Mechanical Properties, and Corrosion Resistance