Abstract:Systematic measurements of stress impedance (SI) and magneto-impedance (MI) have been carried out using Co-rich amorphous ribbons of nominal composition Co71-xFexCr7Si8B14 (x = 0, 2) at various excitation frequencies and bias fields and at room temperature. The impedance, Z, for both the samples was found to be very sensitive functions of applied tensile stress (up to 100MPa) exhibiting a maximum SI ratio as much as 80% at low frequency ~ 0.1MHz. The nature of variation of impedance, Z, changes with the excitation frequency especially at higher frequencies in MHz region where it exhibits a peak. Magnetization measurements were also performed to observe the effects of applied stress and magnetization decreases with the application of stress confirming the negative magnetostriction co-efficient of both the samples. Both the samples exhibited negative magneto-impedance when the variation of Z is observed with the applied bias magnetic field, H. Maximum MI ratio as large as 99% has been observed for both the samples at low fields ~ 27Oe. The impedance as functions of applied magnetic field, Z(H), decreases with the application of stress thus making the MI curves broader. Based on the electromagnetic screening and magnetization dynamics and incorporating the Gilbert and the Bloch-Bloembergen damping and stress dependent anisotropy, the SI has been calculated and is found to describe well the stress and field dependence of impedance of the two samples.

Comparison of Stress-Impedance Effect in Amorphous Ribbons with Positive and Negative Magnetostriction

Experimental Analysis of the Piezomagnetic Properties of Ferromagnetic Steels Subjected to Cyclic Tensile Stress

Stress-Induced Magnetic Hysteresis in Amorphous Microwires Probed by Microwave Giant Magnetoimpedance Measurements

Stress Dependence of Seebeck Coefficient in Iron-Based Amorphous Ribbons

Influence of stress on magneto-impedance in Co71-xFexCr7Si8B14 (x = 0, 2) amorphous ribbons

Stress - and Magneto-Impedance in Co71-xFexCr7Si8B14 (x = 0, 2) amorphous ribbons

Exploring Stress-Dependent Impedance Behavior Via Magnetization Dynamics in Amorphous Magnetic Fibers in High Frequency: Experimental and Modeling

Valve Behavior Of Giant Magnetoimpedance In Field-Annealed Co70fe5si15nb2.2cu0.8b7 Amorphous Ribbon

Stress effect on magnetoimpedance (MI) in amorphous wires at GHz frequencies and application to stress-tunable microwave composite materials

Optimization of magnetoimpedance and stress-impedance effects in single-microwire polymer composites for stress monitoring

Magnetoimpedance Effect in Cobalt-Based Amorphous Ribbons with an Inhomogeneous Magnetic Structure

Evolution of the Magnetic Anisotropy and Magnetostriction in Co-based Amorphous Alloys Microwires Due to Current Annealing and Stress -Sensory Applications

Magnetic anisotropy and stress-magnetoimpedance (S-MI) in current-annealed Co-rich glass-coated microwires with positive magnetostriction

Large GMI effect in Co-rich amorphous wire by tensile stress

Giant Magneto-Impedance and Stress-Impedance Effects of Microwire Composites for Sensing Applications

Giant Stress Impedance Magnetoelastic Sensors Employing Soft Magnetic Amorphous Ribbons

Comparison of magnetoimpedance behaviors in meander CoFeNiSiB amorphous ribbon for deformation sensing applications

Design and characteristic analysis of giant magnetoimpedance sensor in Fe-based nanocrystalline ribbons

Determining the Fatigue Process in Ribbed Steel Bars Using Piezomagnetism

Fatigue, Magnetic and Mechanical Hysteresis

Field/stress Tunable Behaviour of Composites Containing the Combined Current-Modulation Annealed Ferromagnetic Microwires