Abstract:The Ni-Mn-based shape memory alloys as a promising candidate of elastocaloric material has been reported in many literatures, especially on bulk samples. The as-spun ribbon, which has a larger surface area and is more efficient for heat transfer, is rarely studied and hence of importance. In the present work, we succeeded in producing very long as-spun Ni-Fe-Mn-(Al, In) ribbons, with around 300 mm in length. The microstructure and mechanical properties of these as-spun ribbons were thoroughly investigated by scanning electron microscopy / electron backscattered diffraction (SEM/EBSD), nanoindentation and 3-points bending experiments. Through SEM/EBSD analyses, the microstructure and texture of the as-spun ribbons were studied. A gradient in microstructure exists along the thickness direction (TD) of the ribbon, which is induced by the temperature gradient during fast rate solidification, resulting in fine equiaxed grains along the surface contacted with the rotating wheel in melt spinning process and elongated grains, respectively. Both equiaxed and elongated grains possess a strong {001} fiber texture (<001>//TD). Nanoindentation analyses show little variation of hardness between the two different microstructures. The ductility index of both Ni-Fe-Mn-Al and Ni-Fe-Mn-In ribbons are within the range of intermetallic materials. The substitution of In by Al allows to increase very slightly the ductility index, which can reach 0.75. The fine equiaxed grains show better tensile resistance than the elongated grains in 3-points bending test. The substitution of In by Al improves the maximum bending strain by a factor of 3. The maximum strain for Ni-Fe-Mn-Al as-spun ribbons can reach 3 % before fracture. Fractography shows that the intergranular fracture is the main damage mechanism in these as-spun ribbons.

Stress Dependence of Seebeck Coefficient in Iron-Based Amorphous Ribbons

Comparison of Stress-Impedance Effect in Amorphous Ribbons with Positive and Negative Magnetostriction

Effect of Annealing Temperature on Permeability and Giant Magneto-Impedance of Fe-based Amorphous Ribbon

Influence of stress on magneto-impedance in Co71-xFexCr7Si8B14 (x = 0, 2) amorphous ribbons

Evolution of the Magnetic Anisotropy and Magnetostriction in Co-based Amorphous Alloys Microwires Due to Current Annealing and Stress -Sensory Applications

Stress-Induced Magnetic Hysteresis in Amorphous Microwires Probed by Microwave Giant Magnetoimpedance Measurements

Stress - and Magneto-Impedance in Co71-xFexCr7Si8B14 (x = 0, 2) amorphous ribbons

Formation Mechanism of Stress-Induced Anisotropy in Stress-Annealed Fe-based Nanocrystalline Ribbon Alloys

Relating Residual Stress and Microstructure to Mechanical and Giant Magneto-Impedance Properties in Cold-Drawn Co-based Amorphous Microwires

Magnetoimpedance Effect in Cobalt-Based Amorphous Ribbons with an Inhomogeneous Magnetic Structure

Coercivity in stressed amorphous FeCoSiB thin films

Stress-Dependent Magnetization Processes in Cobalt-Based Amorphous Microwires

Special Stress-Magnetization Properties in Co-Based Amorphous Wire

Stable Elastocaloric Effect under Tensile Stress of Iron-Palladium Alloy and Its in Situ X-ray Observation

Effect of CO gas on surface profile and magnetic properties of Fe–Si–B amorphous ribbons

Microstructure and correlated mechanical properties study of Ni-(Fe, Co)-Mn-(Al, In) as-spun ribbons

A Study of the Magnetoelastic Effect in Metallic Textured NiWx (x = 5.5, 6.0, 7.4, and 7.7 at %) Ribbons

Study of dielectric and magnetic properties with Fe76Si19.4Nb2.7Cu1.7P0.2 ribbons

Stress effect on magnetoimpedance (MI) in amorphous wires at GHz frequencies and application to stress-tunable microwave composite materials

Influence of Magneto-Thermal Treatments on Longitudinally Driven Giant Magneto-Impedance Effect in Co-Fe-Si-B Amorphous Ribbons

An Investigation of the Magnetic Domains in the Stressed Amorphous FeCoSiB Magnetoelastic Films