Influence of stress on magneto-impedance in Co71-xFexCr7Si8B14 (x = 0, 2) amorphous ribbons

B.Kaviraj,S.K.Ghatak

DOI: https://doi.org/10.48550/arXiv.cond-mat/0608487

2006-08-23

Abstract:Systematic measurements of stress-impedance (SI) have been carried out using Co-rich amorphous ribbons of nominal composition Co71-xFexCr7Si8B14 (x = 0, 2) at various excitation frequencies and bias fields and at room temperature. The impedance, Z for both the samples was found to be very sensitive functions of applied tensile stresses (up to 100MPa) exhibiting a maximum SI ratio as much as 80% at low frequency ~ 0.1MHz. The nature of variation of SI changes with the excitation frequency especially at higher frequencies in MHz region where it exhibits a peak. Magnetization measurements were also performed to observe the effects of applied stresses and magnetization decreased with the application of stress confirming the negative magnetostriction co-efficient of both the samples. Both the samples exhibited negative magneto-impedance (MI) when the variation of Z is observed with the applied bias magnetic field, H. The impedance as functions of applied magnetic field, Z(H), decreases with the application of stress thus making the MI curves broader. Maximum MI ratio as large as 99% has been observed for both the samples at low fields ~ 27Oe.

Materials Science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to study the influence of stress on the magneto - impedance (MI) effect of Co - based amorphous ribbons (specifically Co\(_{71 - x}\)Fe\(_x\)Cr\(_7\)Si\(_8\)B\(_{14}\), where \(x = 0, 2\)). Specifically, the author explored the following aspects by systematically measuring the stress - impedance (SI) relationships at different frequencies and bias magnetic fields:

1. **Influence of stress on impedance**: How stress changes the impedance characteristics of the material at different frequencies.
2. **Frequency dependence**: The behavior of impedance changing with frequency, especially in the low - frequency and high - frequency regions.
3. **Change in magnetization intensity**: The influence of stress on the magnetization intensity of the sample, especially the role of the negative magnetostrictive coefficient.
4. **Magneto - impedance effect**: The influence of stress on the magneto - impedance effect, including the change of impedance with the applied DC magnetic field.

Through these studies, the author hopes to reveal the specific influence mechanism of stress on the magneto - impedance effect of Co - based amorphous ribbons and provide theoretical basis and technical support for the further application of these materials.

### Main findings

1. **Stress - impedance relationship**:
- At low frequencies (about 0.1 MHz), the impedance decreases significantly with the increase of stress, and the maximum SI ratio can reach 80%.
- At high frequencies (such as 10 MHz), the impedance first increases to a peak value with the increase of stress and then decreases, and shows a positive SI ratio.

2. **Magnetization intensity**:
- The magnetization intensity decreases with the increase of stress, confirming that the sample has a negative magnetostrictive coefficient.

3. **Magneto - impedance effect**:
- The sample shows a large negative magneto - impedance effect at a low magnetic field (about 27 Oe), and the maximum MI ratio can reach 99%.
- Stress broadens the MI curve, and at higher stress, the zero - field impedance value decreases.

### Conclusion

This study shows that stress has a significant influence on the magneto - impedance effect of Co - based amorphous ribbons, specifically:
- The change of impedance with stress depends on the frequency. At low frequencies, the impedance decreases monotonically, while at high frequencies, a peak value appears.
- The negative magnetostrictive coefficient causes the magnetization intensity to decrease with stress, thus affecting the impedance.
- The sample shows a large negative magneto - impedance effect at a low magnetic field, and stress will broaden the MI response.

These results are helpful for understanding the influence mechanism of stress on the magneto - impedance effect and provide important experimental data and theoretical support for the development of high - performance magneto - sensitive materials.