Abstract:Intergranular stress corrosion cracking (IGSCC) of austenitic iron and nickel base alloys continues to affect the availability of boiling water reactors (BWRs) and represents an important consideration when selecting materials for advanced BWRs. For core internal components, like the core shroud, the issues include the SCC resistance of non-sensitized / L-grade stainless steels and the parametric dependencies of all stainless steels to critical variables like corrosion potential, water purity, sensitization, welding, cold work, etc. The overall objectives of this program are to better understand why L-grade stainless steels are apparently more susceptible to IGSCC in core internal applications than anticipated and to guide recommendations for remedial measures if needed. This study focused on the response of sensitized and non-sensitized stainless steels at high and low corrosion potentials, the influence of cold work and the characterization of strains in weld HAZs. Laboratory crack growth rate measurements have produced intergranular rates faster than expected for annealed stainless steel at high potentials and intergranular rates equivalent to thermally sensitized 304 SS when the annealed 304L is cold worked. An electron back scattered pattern technique shows that up to 10% strain from weld shrinkage exists in the weld HAZ of a 304L vertical core shroud weld. These early findings suggest that the combination of high corrosion potential and cold work may be dominant factors in many instances of core shroud cracking. Data to date fully confirm the effectiveness of NobleChem(TM) technology in lowering the corrosion potential and mitigating cracking.

Characterization of Stress Corrosion Cracking Initiation Precursors in Cold-Worked Alloy 690 Using Advanced High-Resolution Microscopy

A High-Resolution Characterization of the Initiation of Stress Corrosion Crack in Alloy 690 in Simulated Pressurized Water Reactor Primary Water

Microstructural Study on the Stress Corrosion Cracking of Alloy 690 in Simulated Pressurized Water Reactor Primary Environment

Stress corrosion crack initiation in Alloy 690 in high temperature water

Comparison of the Stress Corrosion Cracking Growth Behavior of Cold Worked Alloy 690 in Subcritical and Supercritical Water

Effect of Cold Work on the Stress Corrosion Cracking Behavior of Alloy 690 in Supercritical Water Environment

Effect of Intergranular Carbides on the Cracking Behavior of Cold Worked Alloy 690 in Subcritical and Supercritical Water

Insights into the stress corrosion cracking of solution annealed alloy 690 in simulated pressurized water reactor primary water under dynamic straining

Environmentally Assisted Crack Growth in One-Dimensionally Cold Worked Alloy 690tt in Primary Water

The Effects of Grain Boundary Carbide Density and Strain Rate on the Stress Corrosion Cracking Behavior of Cold Rolled Alloy 690

On the role of intergranular nanocavities in long-term stress corrosion cracking of Alloy 690

Characterizing the Effect of Creep on Stress Corrosion Cracking of Cold Worked Alloy 690 in Supercritical Water Environment

Quantitatively evaluating the contribution of intergranular carbides, Cr-depleted zone, and grain boundary to intergranular stress corrosion cracking of Alloy 600 in a simulated boiling water reactors environment with high oxygen concentrations

CRACK GROWTH BEHAVIOR FOR STRESS CORROSION CRACKING OF 690 ALLOY IN HIGH TEMPERATURE WATER

A Novel Test Technique for the Mechanistic Study of Initiation of Environmentally Assisted Cracking on a Ni–30Cr–10Fe Alloy in Simulated Pressurized Water Reactor Primary Water

Strain Rate Dependence of the Effect of Intergranular Carbides on the Resistance to Stress Corrosion Cracking Initiation of Alloy 690 in Simulated Pwr Primary Water

Intergranular Stress Corrosion Cracking Of Unsensitized Stainless Steels In Bwr Environments

Effects of Surface State and Applied Stress on Stress Corrosion Cracking of Alloy 690TT in Lead-containing Caustic Solution

Corrosion Fatigue Crack Growth Behavior of Alloy 690 in High-Temperature Pressurized Water

Insights into stress corrosion cracking in scratched area of alloy 690TT steam generator tubes

The Effect of Cold Rolling on Grain Boundary Structure and Stress Corrosion Cracking Susceptibility of Twins in Alloy 690 in Simulated PWR Primary Water Environment