Preparation and thermal properties of shape‐stabilized polyethylene glycol/mesoporous silica composite phase change materials for thermal energy storage

Chaoming Wang,Zhengyu Cai,Ke Chen,Jun Huang,Tingjun Wang

DOI: https://doi.org/10.1002/est2.45

2019-04-01

Energy Storage

Abstract:Abstract Mesoporous silica (MS) was prepared through a simple self‐assembly procedure under alkaline condition with tetraethyl orthosilicate (TEOS) as SiO 2 precursor and cetyltrimethyl ammonium bromide (CTAB) as the template. A series of shape‐stabilized composite phase change materials (ss‐CPCMs), using polyethylene glycol 6000 (PEG6000) as the PCM and MS as the matrix with different mass percentage of PEG6000 loadings, was prepared through a vacuum impregnation method. N 2 adsorption‐desorption analyzer measurement showed the specific surface area and average pore size of the as‐prepared porous silica were determined to be 760 m 2 /g and about 3 nm, respectively. Differential scanning calorimetry (DSC) measurements indicated that the melting peak temperatures and latent heats of melting of the composites are varied from 52.3°C to 62.6°C and 32.9 to 186.4 J/g (PEG6000 mass fractions: 0%‐80%), which was proportional to PEG6000 content. Fourier‐transform infrared (FT‐IR) spectroscopy results implied that only the physical interaction existed between the PEG6000 and SiO 2 matrix. The shape‐stability measurements suggested the composite with the 70% mass loading of PEG6000 can still maintained the original shape and no leakage were observed above the much higher melting temperature of PEG6000 (105°C). Thermal cycling test showed that the ss‐CPCM had good thermal reliability and chemical stability although it was experienced 500 melting and cooling cycles. Moreover, the thermal decomposition temperature of the composites (393.2°C) was much larger than the melting temperature of pure PEG6000 (62.6°C), which indicated that composite presented excellent thermal stabilities and was suitable for thermal energy storage applications.