Abstract:Abstract Mesoporous silica (MS) was prepared through a simple self‐assembly procedure under alkaline condition with tetraethyl orthosilicate (TEOS) as SiO 2 precursor and cetyltrimethyl ammonium bromide (CTAB) as the template. A series of shape‐stabilized composite phase change materials (ss‐CPCMs), using polyethylene glycol 6000 (PEG6000) as the PCM and MS as the matrix with different mass percentage of PEG6000 loadings, was prepared through a vacuum impregnation method. N 2 adsorption‐desorption analyzer measurement showed the specific surface area and average pore size of the as‐prepared porous silica were determined to be 760 m 2 /g and about 3 nm, respectively. Differential scanning calorimetry (DSC) measurements indicated that the melting peak temperatures and latent heats of melting of the composites are varied from 52.3°C to 62.6°C and 32.9 to 186.4 J/g (PEG6000 mass fractions: 0%‐80%), which was proportional to PEG6000 content. Fourier‐transform infrared (FT‐IR) spectroscopy results implied that only the physical interaction existed between the PEG6000 and SiO 2 matrix. The shape‐stability measurements suggested the composite with the 70% mass loading of PEG6000 can still maintained the original shape and no leakage were observed above the much higher melting temperature of PEG6000 (105°C). Thermal cycling test showed that the ss‐CPCM had good thermal reliability and chemical stability although it was experienced 500 melting and cooling cycles. Moreover, the thermal decomposition temperature of the composites (393.2°C) was much larger than the melting temperature of pure PEG6000 (62.6°C), which indicated that composite presented excellent thermal stabilities and was suitable for thermal energy storage applications.

Carbon layer-modified mesoporous silica supporter for PEG to improve the thermal properties of composite phase change material

Efficient Shape-Stabilized Phase-Change Material Based on Novel Mesoporous Carbon Microspheres As a Matrix for Polyethylene Glycol: Preparation and Thermal Properties

Novel PEG/SiO2/SiO2–modified expanded graphite composite phase change materials for enhanced thermal energy storage performance

Preparation and thermal properties of shape‐stabilized polyethylene glycol/mesoporous silica composite phase change materials for thermal energy storage

Polyethylene glycol/silica (PEG@SiO2) composite inspired by the synthesis of mesoporous materials as shape-stabilized phase change material for energy storage

Using mesoporous carbon to pack polyethylene glycol as a shape-stabilized phase change material with excellent energy storage capacity and thermal conductivity

Enhanced thermal properties of novel shape-stabilized PEG composite phase change materials with radial mesoporous silica sphere for thermal energy storage

Design and Preparation of Novel Shapeable PEG/SiO2/AA Shape-Stabilized Phase Change Materials Based on Double-Locked Network with Enhanced Heat Storage Capacity for Thermal Energy Regulation and Storage

The Shape-Stabilized Phase Change Materials Composed Of Polyethylene Glycol And Various Mesoporous Matrices (Ac, Sba-15 And Mcm-41)

Cost-Effective Biochar Produced from Agricultural Residues and Its Application for Preparation of High Performance Form-Stable Phase Change Material via Simple Method

Silver microsphere doping porous-carbon inspired shape-stable phase change material with excellent thermal properties: preparation, optimization, and mechanism

Polyethylene Glycol Confined in SiO2-Modified Expanded Graphite as Novel Form-Stable Phase Change Materials for Thermal Energy Storage

Copper Microsphere Hybrid Mesoporous Carbon As Matrix for Preparation of Shape-Stabilized Phase Change Materials with Improved Thermal Properties

Effects of carbonization temperature on the thermal characteristics of shape-stable composite phase change materials based on silica aerogel

Phase Change Materials Based on Polyethylene Glycol Supported by Graphene-Based Mesoporous Silica Sheets

Shape–stabilized phase change materials composed of polyethylene glycol and ordered mesoporous silica synthesized from fly ash

Preparation and Thermal Properties of Novel Shape-Stabilized Phase Change Materials Based on Polyethylene Glycol/Meso-Structured Onion-Like Silica Composite

Stable and reliable PEG/TiO2 phase change composite with enhanced thermal conductivity based on a facile sol-gel method without deionized water

High thermal conductivity and low leakage phase change materials filled with three-dimensional carbon fiber network

Double-skeleton based shape-stabilized phase change materials with excellent solar-thermal energy conversion and shape memory performance

Polyethylene Glycol–Calcium Chloride Phase Change Materials with High Thermal Conductivity and Excellent Shape Stability by Introducing Three-Dimensional Carbon/Carbon Fiber Felt