Comparative study of laser surface hardening of 50CrMo4 steel using continuous-wave laser and pulsed lasers with ms, ns, ps and fs pulse duration

Niroj Maharjan,Wei Zhou,Yu Zhou,Yingchun Guan,Naien Wu

DOI: https://doi.org/10.1016/j.surfcoat.2019.03.036

IF: 4.865

2019-05-01

Surface and Coatings Technology

Abstract:Laser surface hardening, used to achieve hardened surface without affecting bulk properties of steels, generally employs continuous-wave laser to do the job. The purpose of this paper is to systematically investigate the use of different pulsed lasers for surface hardening of 50CrMo4 steel. A continuous-wave laser and various pulsed lasers with pulse duration ranging from fs to ms were used for the experiment. It was found that millisecond laser utilizing about 9 times lower power is as effective as continuous-wave laser for surface hardening. It produced an average surface hardness of ~719 HV (2.7 times higher than base material hardness) and ~200 μm hardened depth, which is comparable with continuous-wave laser hardening. Similarly, nanosecond laser could induce both surface hardening effect and material removal depending on the parameters used. However, a shallow hardened depth (of mere ~80 μm) was achieved compared to continuous-wave laser. Furthermore, femtosecond and picosecond lasers did not produce any observable surface hardening effect; instead they resulted in direct surface ablation.

physics, applied,materials science, coatings & films