Abstract:In this work, the most efficient and common engineered surface treatments identified as shot peening (SP), laser shock peening (LSP) and ultrasonic surface rolling process (USRP) were utilized to impact the 300 M ultrahigh strength steel. The microstructure evolution and surface strengthening behavior were carefully characterized and compared for the 300 M steel with various treatments. Besides, the underlying mechanisms for difference in grain refinement and surface mechanical properties by the arranged surface modification are revealed. The results indicate that a gradient structure with nano-grains at the top surface appears on the SP, LSP and USRP treated samples. The process of repeated impacts of SP in different directions leads to activation of multiple slip systems, which thus causes severe refined grains and dense dislocation activities associated with dislocation tangles, dislocation walls and blocking. A great variety of strikes per unit area by USRP results in higher plastic deformation compared to SP where numerous dislocation cells and deformation bands were generated. In contrast to SP and USRP, fewer slip systems are activated in LSP due to the short duration time which thus leads to the thinnest refined grain layer and more planar dislocation structures. The combination of low plastic work and lack of refined grains leads to lowest full width at half maximum (FWHM) in case of LSP samples whereas high FWHM comes from both fine grain size and dislocations in SP. The grain refinement and plastic work contributes to an increase of microhardness and compressive residual stress for the SP, LSP and USRP samples. To be clear, SP leads to a higher magnitude of hardness and compressive residual stress on the topmost surface while LSP causes a larger depth due to that shock wave in LSP influences material to much greater depth. Besides, the decomposition and redistribution of carbides are also noticed on the surface layer after the surface treatments with very high strain rate where numerous dislocations accumulate at the border of the carbides and slip trace is also observed within the carbides.

Steel Surface Modification with Carbon Nanomaterial Using Concentrated Energy Flows

Strain-induced Refinement and Thermal Stability of a Nanocrystalline Steel Produced by Surface Mechanical Attritiontreatment

Electron-Beam Modification of Carbon Steel Surface

Microstructure and Hardness Analysis of Carbon Nanotube Cladding Layers Treated by Laser Beam

The Effects of Laser‐Assisted Ultrasonic Nanocrystal Surface Modification on the Microstructure and Mechanical Properties of 300M Steel

Features of Steel Structure Formation in Areas of High-Speed Laser Hardening from Liquid State

Modification of Structure and Properties of Surfacing of High-Speed Steel by Electron-Beam Treatment

Surface modification of mild steel using a combination of laser and electrochemical processes

Surface Hardening of 30crmnsia Steel Using Continuous Electron Beam

Surface Modification of Mild Steel by Carbon Nanotubes Reinforcement under Electron Beam Melting

Structure and Wear Resistant Behavior of Laser Strengthening Carbon Nanotubes Coating on Steel Surface

Influence of the initial structure on the efficiency of laser processing of steel

Surface Modification of Steels and Magnesium Alloy by High Current Pulsed Electron Beam

Electron beam hardening of nanobainitic steel

Maraging Steel Laser Additive Manufacturing Process and Microstructure Study

Microstructure evolution and surface strengthening behavior of 300 M ultrahigh strength steel under engineered surface treatments

Local laser softening of press-hardened steel at high feed rates

Microstructure and Wear Property of Carbon Nanotube Carburizing Carbon Steel by Laser Surface Remelting

Local laser softening of high-strength steel with an adapted intensity

Effect of laser surface hardening on a low carbon steel substrate wear and hardness

Microstructure and Hardness of the Laser Surface Treated Titanium