Abstract:Stress relaxation cracking (SRC) is considered one of the major failure mechanisms for 347H stainless steel welds at elevated service temperatures or during post weld heat treatment (PWHT), especially within the heat-affected zone (HAZ). This work focuses on the characterization of SRC susceptibility within 347H physically simulated arc welded HAZ at elevated temperatures. A four-step SRC thermomechanical test in combination with finite element modeling (FEM) of the welding and testing processes is developed to establish a susceptibility map for HAZ. The test first runs a thermal cycle with three different peak temperatures (1335, 1275, and 1150 °C) to duplicate representative HAZ subzone microstructures, followed by time-to-failure examination under a variety of pre-stress (260–600 MPa) and pre-strain conditions (0.03–0.19) as a function of reheat temperatures between 750 and 1050 °C. With the aid of FEM, SRC susceptibility maps are generated to identify the threshold stress, plastic strain, and creep strain as a function of test temperature. It was found out that HAZ subzone with a lower peak temperature (1150 °C) appears to be slightly less susceptible to SRC than the other two subzones that experienced higher peak temperatures. Generally, time-to-fracture reduces with increasing initially applied stress and strain for all test temperatures. The pre-stress thresholds decrease from about 500 to 330 MPa as the testing temperature increases from 800 to 1050 °C, while the corresponding initial plastic strain thresholds reduces from 0.15 to 0.06. The SRC susceptibility was also evaluated through the Larson–Miller Parameter (LMP) analysis as a function of plastic strain, initial stress and starting stress upon reaching the testing temperature, respectively. The 1050 °C test with a high pre-applied strain (0.1) exhibits an extremely short time to failure (t = 3 s) that lies outside the general trend in LMP analysis. Additionally, it was identified that a plastic strain above 0.07 is identified to significantly reduce the bulk creep strain tolerance to fracture and therefore increases SRC susceptibility. Hardness measurement and fractography analysis indicated that the strain aging of niobium carbonitrides and other potential phases in conjunction with intergranular precipitates contributes to an increase in microhardness and increased intergranular cracking susceptibility.

Stress-Corrosion Cracking Failure of a Sensitized Valve Stem

The Stress Corrosion Cracking of Austenitic Stainless Steel Heat Exchange Tubes: Three Cases Study

Fracture analysis of high pressure main steam valve stem of a 300 MW steam turbine

Intergranular Fatigue Cracking of a Stainless Steel Expansion Joint

Stress Relaxation Cracking in 347H Stainless Steel Arc Welds: Susceptibility Evaluation of Heat-Affected Zone

Insight into the stress corrosion cracking of HP-13Cr stainless steel in the aggressive geothermal environment

Stress corrosion crack initiation in Alloy 690 in high temperature water

Towards Understanding Stress Corrosion Cracking of Austenitic Stainless Steels Exposed to Realistic Sea Salt Brines

Stress Corrosion Cracking of 60/40 Cupro-Nickel Alloy: Fractography and Chemical Analysis

Investigations on the SCC initiation behavior of cold worked 316L in high temperature oxygenated water at constant loads

Analysis of Cracking of Pressure Gauge Spring Tube for Hydrogenation Plant

Weld Cracking of a Stainless Steel Heat Exchanger

Chloride-Induced Stress Corrosion Cracking of Friction Stir-Welded 304L Stainless Steel: Effect of Microstructure and Temperature

Stress Corrosion Cracking of Heat Exchanger Tubes in District Heating System

Corrosion crack failure analysis of 316L hydraulic control pipeline in high temperature aerobic steam environment of heavy oil thermal recovery well

Stress corrosion cracking of leaded brass used in oil temperature sensor of vehicle

Stress corrosion cracking behavior of super 13Cr tubing in phosphate packer fluid of high pressure high temperature gas well

Investigation of Multi-Factor Stress Corrosion Cracking Failure of Safe-End Feedwater Lines of Submarine Power System

Effect of Precipitate on Thermal Aging Effect of 17-4PH Martensitic Stainless Steel Used as Valve Stem in Nuclear Power Plant

Fracture Mechanics Analysis Of The Stress Corrosion Cracking Failure Of Stainless Steel Hexagonal Head Screws In A Marine-Industrial Environment

Failure analysis on fracture causes of stainless-steel studs in seawater system of nuclear power plants