Abstract:Ceramic Li6.55Al0.2La3Zr2O12 (LLZO) is one of the most attractive electrolyte materials for solid-state batteries that combined with metallic Li anodes holds the promise for safer and more energetically dense battery, but its performance is limited by the increases in electrolyte-electrode interfacial resistances upon cycling. The combination of Li + -conducting ceramics and polymers offers a new pathway to create better electrolytes with both high ionic conductivity and good (electro)mechanical interfacial properties. We optimized two-step annealing processing conditions for the fabrication of low temperature cubic-LLZO nanofibers and Li 2 CO 3 removal from the surface of the nanofibers. Using industrially relevant roll-to-roll electrospinning and slot-die coating, we fabricated thin composite membranes with reproducible thickness down to 50 microns. We investigated PEO based composite polymer electrolyte (CPE) with a high, 50 wt% loading of Al-doped LLZO nanofibers in comparison with nanofiber-free PEO electrolyte. XPS measurements show that LLZO is not present at the composite electrolyte surface, and solid electrolyte interphase (SEI) formation is dictated solely by PEO and LiTFSI when reacting with Li metal. Electrochemical SEI formation, studied by cyclic voltammetry, shows SEI formation is identical with and without up to 75 wt% LLZO in the electrolyte. Galvanostatic cycling with lithium symmetric cells shows that the critical current density (CCD) can be tripled by including 50 wt% LLZO, but half cell cycling reveals this comes at the cost of CE. Varying the LLZO loading shows that even a small amount of LLZO drastically lowers the CE, from 88% at 0 wt% LLZO to 77% at just 2 wt% LLZO. Mesoscale modelling reveals that the increase in CCD cannot be explained by an increase in the macroscopic or microscopic stiffness of the electrolyte; only the microstructure of the LLZO nanofibers in the PEO-LiTFSI matrix slows dendrite growth by presenting physical barriers that the dendrites must push or grow around. This tortuous lithium growth mechanism around the LLZO is corroborated with mass spectrometry imaging. Electrochemical impedance spectroscopy (EIS) analysis showed comparable bulk ionic and interfacial resistances with and without nanofibers, indicating that PEO dominates Li + transport and interfacial chemistry. The total Li-ion conductivity of the composite is still governed by the polymer matrix due to high interfacial resistance between the garnet particles and the PEO/LiTFSI matrix. This work highlights important elements to consider in the design of CPEs for high-efficiency lithium metal batteries.

Effect of titanium dioxide and zinc oxide fillers on morphology, electrochemical and mechanical properties of the PEO-based nanofibers, applicable as an electrolyte for lithium-ion batteries

Preparation and characterization of PEO-PMMA polymer composite electrolytes doped with nano-Al 2 O 3

The “filler effect”: A study of solid oxide fillers with β-Li3PS4 for lithium conducting electrolytes

Effects of the Shapes of BaTiO3 Nanofillers on PEO-based Electrolytes for All-Solid-state Lithium-Ion Batteries

Role of Filler Content and Morphology in LLZO/PEO Membranes

Electrospun PEO nanofibrous membrane enable by LiCl, LiClO4, and LiTFSI salts: a versatile solvent-free electrolyte for lithium-ion battery application

Evaluation of high-entropy (Cr, Mn, Fe, Co, Ni)-oxide nanofibers and nanoparticles as passive fillers for solid composite electrolytes

Enhanced electrical properties of spun blend polymer composite electrolyte PMMA – PVdF-co-HFP – PEO/ LiBF4 containing nano SiO2 for lithium-ion batteries application

Electrospun Poly(ethylene Oxide) Nanofibrous Composites with Enhanced Ionic Conductivity As Flexible Solid Polymer Electrolytes

Ternary metal oxide filled PEO-based polymer electrolyte for solid-state lithium metal battery: The role of filler particle size

Influence of TiO2 nano-particles on the transport properties of composite polymer electrolyte for lithium-ion batteries

Electrospun Polyethylene Oxide (PEO)-Based Composite polymeric nanofiber electrolyte for Li-Metal Battery

Effect of Organic Functional Groups on Poly(ethylene Oxide) Electrolytes for High-Performance Solid-State Lithium-Metal Batteries

LiTFSI salt concentration effect for well‐balanced ion transport and physical properties in nanocellulose‐reinforced PEO#600 solid electrolytes

The Effects of Electrospinning Structure on the Ion Conductivity of PEO-Based Polymer Solid-State Electrolytes

Ion-conductive vs. non-ion-conductive ceramic fillers in silane-linked polyethylene oxide-based composite polymer electrolytes with high room-temperature ionic conductivity

(Invited) Advancing Understanding of Composite Polymer Electrolytes with LLZO Nanofibers

Li0.33La0.557TiO3 Ceramic Nanofiber-Enhanced Polyethylene Oxide-Based Composite Polymer Electrolytes for All-Solid-state Lithium Batteries

Electrochemical and Nanomechanical Properties of TiO 2 Ceramic Filler Li‐Ion Composite Gel Polymer Electrolytes for Li Metal Batteries

Enhanced electrochemical properties of PEO-based composite polymer electrolyte with shape-selective molecular sieves

Dielectric polarization and relaxation processes of the lithium-ion conducting PEO/PVDF blend matrix-based electrolytes: effect of TiO2 nanofiller