Unified understanding and mitigation of detrimental phase transition in cobalt-free LiNiO 2
Itsuki Konuma,Naohiro Ikeda,Benoît D.L. Campéon,Hinata Fujimura,Jun Kikkawa,Huu Duc Luong,Yoshitaka Tateyama,Yosuke Ugata,Masao Yonemura,Toru Ishigaki,Taira Aida,Naoaki Yabuuchi
DOI: https://doi.org/10.1016/j.ensm.2024.103200
IF: 20.4
2024-01-20
Energy Storage Materials
Abstract:Ni-enriched layered materials are used as electrode materials of Li-ion batteries for electric vehicle applications. Stoichiometric LiNiO 2 with cationic Ni 3+ /Ni 4+ redox is the ideal electrode material, but the gradual loss of capacity at the high voltage region, associated with Ni ion migration, hinders its use for practical applications. Therefore, to improve electrode reversibility of LiNiO 2 , less abundant Co ions and/or other electrochemically inactive ions, e.g ., Al 3+ ions, are in part substituted for Ni ions. Nevertheless, a unified understanding of improvement by metal substitution is as yet not established. In this study, the origin causing detrimental phase transition in LiNiO 2 is discussed through the detailed analysis on LiNiO 2 integrated with nanosized Li 3 PO 4 derived from a metastable and rocksalt LiNiO 2 –Li 3 PO 4 solid solution sample. LiNiO 2 derived from the metastable rocksalt oxide has approximately 6 % anti-site defects, and the particle size growth is suppressed by uniformly dispersed nanosized Li 3 PO 4 . In low crystallinity LiNiO 2 with partial structural disordering, the Ni ion migration to tetrahedral sites is effectively suppressed because of repulsive electrostatic interaction from Ni ions in Li layers. Moreover, from these findings, non-stoichiometric Li 0.975 Ni 1.025 O 2 with smaller particle size has been directly synthesized without high-energy milling and Li 3 PO 4 integration, and significant improvement of electrode reversibility is achieved. Electrode reversibility of non-stoichiometric Li 0.975 Ni 1.025 O 2 is further improved through surface stabilization in a highly concentrated electrolyte solution. The unified understanding of deterioration mechanisms for LiNiO 2 offers a new criterion to design Co-free LiNiO 2 without metal substitution, leading to full utilization of a reversible capacity for layered materials.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology