Abstract:The fatigue fracture behavior of four ultrahigh strength steels with different melting processes and therefore different inclusion sizes were studied by using a rotating bar two-point bending fatigue machine in the high-cycle regime Up to 10(7) cycles of loading. The fracture surfaces were observed by field emission scanning electron microscopy (FESEM). It was found that the size of inclusion has significant effect on the fatigue behavior. For AISI 4340 steel in which the inclusion size is smaller than 5.5 mu m, all the fatigue cracks except one did not initiated from inclusion but from specimen surface and conventional S-N curve exists. For 65Si2MnWE and Aermet 100 steels in which the average inclusion sizes are 12.2 and 14.9 mu m, respectively, fatigue cracks initiated from inclusions at lower stress amplitudes and stepwise S-N curves were observed. The S-N curve displays a continuous decline and fatigue failures originated from large oxide inclusion for 60Si2CrVA steel in which the average inclusion size is 44.4 mu m. In the case of internal inclusion-induced fractures at cycles beyond about 1x10(6) for 65Si2MnWE and 60Si2CrVA steels, inclusion was always found inside the fish-eye and a granular bright facet (GBF) was observed in the vicinity around the inclusion. The GBF sizes increase with increasing the number of cycles to failure N-f in the long-life regime. The values of stress intensity factor range at crack initiation site for the GBF are almost constant with N-f, and are almost equal to that for the surface inclusion and the internal inclusion at cycles lower than about 1x10(6). Neither fish-eye nor GBF was observed for Aermet 100 steel in the present study.

Effect of Nonmetallic Inclusions on Fatigue Properties of Superelastic Ti-Ni Fine Wire

Effect of Heat Treatment on Fatigue Behaviour of Biomedical Ni–Ti Alloy Wires under Ultrasonic Conditions

The Effect of Inclusions on the Fatigue Behavior of Fine-Grained High Strength 42crmovnb Steel

Influence of Non-Metallic Inclusions on Very High-Cycle Fatigue Performance of High-Strength Steels and Interpretation via Crystal Plasticity Finite Element Method

Effects of Ce-Modified TiN Inclusions on the Fatigue Properties of Gear Steel 20CrMnTi

Influence of Non-Metallic Inclusions on Bending Fatigue Strength of High-Quality Carbon Constructional Steel Heated in an Industrial Electric Arc Furnace

Effect of Non-metallic Inclusions on the Local Stress Concentration Within Materials

High cycle fatigue behavior of titanium microalloyed high-strength beam steels

Effect of Pre-Added HfO2 Inclusions on Carbide Morphology and Deformation Behavior in DZ125 Nickel-Based Superalloy

Fracture Mechanisms Induced by Microporosity and Precipitates in Isothermal Fatigue of Polycrystalline Nickel Based Superalloy

Effect of carbon addition on the microstructure and mechanical behavior of near equiatomic NiTi alloy wire

A Fatigue Life Model for Predicting Crack Nucleation at Inclusions in Ni-Based Superalloys

Research progress in influence of non-metallic inclusion characteristics on fatigue properties of iron and steel materials

Influence of Inclusion Size on Fatigue Behavior of High Strength Steels in the Gigacycle Fatigue Regime

High-Cycle Fatigue Fracture Behavior of Ultrahigh Strength Steels

Effects of Ni Content on Low Cycle Fatigue and Mechanical Properties of Al-12Si-0.9Cu-0.8Mg-xNi at 350 °C

Study on Micro-Mechanism of Crack Initiation and Propagation Induced by Inclusion in Ultra-High Strength Steel

Sem in Situ Observations to the Effects of Inclusions on Initiation and Propagation of the Low Cyclic Fatigue Crack in Super Strength Steel

Study on Tensile and Thermal Fatigue Behaviors of Additively Manufactured Cobalt-Based Alloys Alloying with Al and Ni

Effect of Inclusion Size and Distribution on Low Cycle Fatigue Properties of an FGH97 Superalloy

Frequency effect on low‐cycle fatigue behavior of pseudoelastic NiTi alloy