Tensile Fracture Behavior and Characterization of Ceramic Matrix Composites

Jeongguk Kim

DOI: https://doi.org/10.3390/ma12182997

IF: 3.4

2019-09-16

Materials

Abstract:Tensile fracture behavior of ceramic matrix composites (CMCs) was investigated using characterization tools. First, a high-speed infrared camera was used to monitor the surface temperature of the CMC specimen during mechanical testing. An infrared camera is a tool used to detect infrared (IR) radiation emitted from a specimen as a function of temperature, and it was used to analyze the temperature monitoring of specimen surface and fracture behavior during the tensile test. After the test, the microstructural analysis using SEM was performed. SEM analysis was performed to investigate the fracture mode and fracture mechanism of CMC materials. In this paper, it was found that the results of the surface temperature monitoring obtained from IR thermal imaging technology and the failure mode analysis obtained through SEM were in a good agreement. These techniques were useful tools to explain the mechanical behavior of ceramic matrix composites. The detailed experiments and testing results will be provided.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to study the fracture behavior of ceramic matrix composites (CMCs) under tensile loads and gain an in - depth understanding of their failure mechanisms through multiple characterization methods. Specifically, the main objectives of this study include:

1. **Study the uniaxial tensile fracture characteristics of ceramic matrix composites**:
- Through experimental testing and data analysis, understand the stress - strain behavior and fracture characteristics of CMCs during the tensile process.

2. **Use infrared thermal imaging technology to monitor the temperature change of specimens**:
- During the tensile test, use a high - speed infrared camera to monitor the surface temperature change of the specimen in real - time to analyze the relationship between temperature change and mechanical properties.

3. **Analyze fracture characteristics through SEM microstructure characterization**:
- Use a scanning electron microscope (SEM) to perform microstructure analysis on the specimens after fracture to determine the fracture mode and fracture mechanism.

4. **Provide a basis for material design**:
- Through the above research, provide detailed fracture characteristic data to provide a scientific basis for the design and application of ceramic matrix composites.

### Summary of Key Issues

- **Material Brittleness Problem**: Traditional ceramic materials are limited in practical applications due to their brittleness. By introducing continuous fiber reinforcement, the fracture toughness of ceramic matrix composites can be improved.

- **Understanding of Fracture Mechanisms**: By combining infrared thermal imaging technology and SEM analysis, the fracture mechanisms of CMCs under tensile loads are revealed, especially the relationship between temperature change and the fracture process.

- **Application of Non - Destructive Testing Technology**: Verify that the high - speed infrared camera is an effective non - destructive evaluation (NDE) tool for monitoring the temperature change and failure process of materials during tensile tests.

### Formula Explanation

Although no complex mathematical formulas are involved in this paper, when describing the stress - strain behavior of materials, the following formula can be used to represent the relationship between stress \(\sigma\) and strain \(\epsilon\):

\[
\sigma = E\cdot\epsilon
\]

where:
- \(\sigma\) is stress (Pa)
- \(E\) is elastic modulus (Pa)
- \(\epsilon\) is strain (dimensionless)

In addition, the ultimate tensile strength (UTS) mentioned in the paper is also an important parameter for evaluating the maximum load - bearing capacity of materials.