Abstract:Due to the randomness of hard and brittle material damage evolution, assessing damage and interpreting mechanisms is challenging. This study focuses on analyzing material damage mechanisms by employing extensive multi-source heterogeneous data to extract quantitative information. A machine vision-based method for detecting and assessing defects in ceramics was proposed, achieving 98 % accuracy. Leveraging this method in scratching experiments, the progression of damage and micro-failure mechanisms in Si3N4 was investigated through the analysis of defect area distribution, force and acoustical signals. Results revealed that the distribution of defect areas conforms to a three-parameter Weibull distribution. At scratch depths of 0.01, 0.02 mm, approximately 90 % of damage accumulated within 1e2–1e4 μm 2 ; conversely, 0.03–0.06 mm led to a decrease to 30 – 40 %. Extensive crack propagation occurs within 0.02–0.03 mm, resulting in the intersecting formation of spalling blocks. Damage evolution occurs in three stages: shallow and small cracks with scattered spalling blocks in the first stage, deep and long cracks with continuous and irregularly shaped spalling blocks in the second stage, and nearly no cracks with continuous and regularly shaped blocks in the third stage. This study not only proposes an efficient method to detect and evaluate ceramic defects, but also deeply understands the evolution process of material damage mechanism. Considering defect distribution and statistical trends, this research not only provide guidance for the optimization of machining parameters, especially in the scene of specific precision and high removal rate. At the same time, the damage evolution and failure mechanism of Si 3 N 4 provide useful experimental basis and data support for deepening the understanding of material behavior during ultra-precision grinding.

Characterization of deformation and damage process of alumina-based ceramics by DIC technique

Deformation and Fracture of Corundum Ceramics with a Multilevel Pore Structure

Method of Damage Characterization of Engineering Ceramics Grinding Surface

In Situ Investigation of Strain Localization in Sintered, Porous Segmented Alumina

Plastic Deformation and Sintering of Alumina under High Pressure

Effect of Pore Size on the Mechanical Properties and Deformation Behavior of Porous ZrO2 (Y2O3) Ceramics Under Axial Compression

Damage Monitoring of Ceramic Matrix Composites Under Tension Loading Via NDE-based DIC Approach

Compressive Strength and Damage Mechanisms in Ceramic Materials. I. The Role of Subcritical Tensile Microfracture Processes in Compression Failure of Ceramics. II. Electron Channeling Study of Fracture in Alumina-Evidence for Crack Tip Plasticity.

Quantification of micro-damage evolution process in ceramics through extensive analysis of multi-source heterogeneous data

Damage and failure analysis of a SiCf/SiC ceramic matrix composite using digital image correlation and acoustic emission

Characterization Methods of Pores in Ceramics and Their Analysis

Application of microtomography and image analysis to the quantification of fragmentation in ceramics after impact loading

Microstructure and Mechanical Properties of Porous Alumina Ceramics Fabricated by the Decomposition of Aluminum Hydroxide

Microstructures and mechanical properties of additively manufactured alumina ceramics with digital light processing

In situ Observation of Compression Damage in a Three-Dimensional Braided Carbon Fiber Reinforced Carbon and Silicon Carbide (C/C-SiC) Ceramic Composite

Combination of Digital Image Correlation (DIC) and in situ 3D-μ-CT in the analysis of the relationship between strains and porosity under creep loading

Fractal characterization of ceramic crack patterns after thermal shocks

Effect of Grain Size on Hertzian Contact Damage in Alumina

Analysis of mechanical behaviour and fracture interaction of multi-hole rock mass with DIC measurement

Numerical Simulation of Sintering of DLP Printed Alumina Ceramics