Abstract:Carbon fibre reinforced silicon carbide (C/SiC) ceramic matrix composites have attracted considerable attention due to their exceptional properties and extensive potential applications as high-temperature structural materials. However, due to their complex structure and manufacturing defects, C/SiC composites exhibit intricate mechanical behaviour under thermal-mechanical-oxidative coupling environments. To date, systematic studies on the internal damage evolution and failure mechanisms of C/SiC composites under high-temperature oxidative environments are lacking. In this study, a combination of synchrotron X-ray micro-computed tomography (SR mu CT) and in-situ experiments under thermal-mechanical-oxidative coupling environments at room temperature and 1650 degrees C in air was used to characterize the internal microstructures and damage evolution processes of C/SiC composites at different loading levels. Additionally, the 3D strain fields during in-situ loading were quantitatively analysed using the Digital Volume Correlation (DVC) method. The findings underscore the substantial impact of oxidative damage on the mechanical response of C/SiC composites, particularly concerning tensile properties and fracture modes. At room temperature, severe delamination, fibre bundle pull-out and interfacial debonding occurred internally. Whereas, under high-temperature atmospheric conditions, severe fibre oxidation reactions occurred at the specimen edges, resulting in rapid porosity escalation. Crack initiation from surface defects followed by rapid inward propagation is observed. Moreover, while the strain distribution remains relatively uniform until fracture, a pronounced concentration of strain is evident near the fracture zones at room temperature, with an even greater concentration observed at 1650 degrees C. Notably, the region of concentrated strain within the 3D deformation field corresponds closely to the final fracture location, as revealed by quantitative DVC analysis.

Application of microtomography and image analysis to the quantification of fragmentation in ceramics after impact loading

Microdamage In Polycrystalline Ceramics Under Dynamic Compression And Tension

Damage of 2D-Sic/sic Composites under Projectile Impact and Tensile Properties after Impact

Experimental and theoretical investigation of failure mechanism in Al 2 O 3 /SiC composite under plane shock waves

Micro-structure response and fracture mechanisms of C/SiC composites subjected to low-velocity ballistic penetration

Cone cracking and fragmentation of alumina plates under high-speed penetration: Experiments and modelling

Progressive Fragment Modeling of Failure Wave in Ceramics under Planar Impact Loading

Studying SiC/SiC Composites by X-Ray Tomography

Probabilistic estimation of impact fracture strength of ceramics.

In situ characterization of foreign object damage (FOD) in environmental-barrier-coated silicon carbide (SiC) ceramic

Simulation of microplasticity-induced deformation in uniaxially strained ceramics by 3-D Voronoi polycrystal modeling

Quantification of micro-damage evolution process in ceramics through extensive analysis of multi-source heterogeneous data

Dynamic Fragmentation of Ceramics Based on Carbon and Silicon Carbide

Dynamic Fracture Process and Strain Rate Effect of a Porous SiC Ceramic

Real-time visualization of impact damage in monolithic silicon carbide and fibrous silicon carbide ceramic composite

Analysis of the Damage Initiation in a SiC/SiC Composite Tube from a Direct Comparison Between Large-Scale Numerical Simulation and Synchrotron X-ray Micro-Computed Tomography

Internal Damage Evolution of C/SiC Composites in Air at 1650 °C Studied by In-Situ Synchrotron X-ray Imaging

Computational investigation of the dynamic response of silicon carbide ceramic under impact loading

Effects of microstructures on the fracture properties of silicon nitride ceramics at elevated temperatures

A Shockless Plate-Impact Spalling Technique, Based on Wavy-Machined Flyer-Plates, to Evaluate the Strain-Rate Sensitivity of Ceramic Tensile Strength

Rapid geometric characterization of ceramics fragments through split Hopkinson pressure bar tests