Abstract:There is a great potential in using different techniques of additive manufacturing (AM) for the production and refurbishment of hot forming dies. In hot stamping of AlSi-coated boron steel, the dies are exposed to a complex combination of abrasive and adhesive wear. This results in tool damage and eventually tool refurbishment is necessary. Laser-metal-deposition (LMD) is an AM technique suitable for tool repairing due to its easier implementation, compared to selective-laser-melting (SLM). However, tribological studies on AM produced tools are still limited, particularly in the context of hot forming. Thus, the aim of this work is to increase the knowledge on the friction and wear behavior of LMD tool materials in hot stamping conditions. Two LMD materials were investigated: a hot-work tool steel (LMD-TS) and a conceptual high-hardness tool material (LMD-HH). Porosity was observed for both materials in the form of lack-of-fusion defects. LMD-TS resulted in a Vickers hardness value of approximately 650 HV, while LMD-HH showed a value of approximately 1100 HV. A high temperature strip drawing tribometer was used to perform friction and wear tests against AlSi-coated boron steel under unidirectional (linear) sliding conditions. Workpiece temperatures during sliding were 600°C and 700°C. All tribotests at 700°C resulted in severe adhesion and AlSi-coating rupture, resulting in higher and more unstable friction. The wear mechanisms observed for LMD-TS were a combination of abrasive and adhesive wear, where ploughing and grooving in the tool material resulted in larger surface defects to accumulate material transfer. At 700°C, these mechanisms were more severe. LMD-HH did not show significant abrasive damage in any test; the resulting material transfer was thinner and sparser compared to the other LMD material. The change in FeAlSi material transfer for LMD-HH was associated with the reduction in abrasive damage, i.e., ploughing and grooving in the tool material did not take place and thus did not enhance material transfer. The LMD process itself did not seem to have either a positive or a negative effect on the tribological behavior of the tool materials in this tribosystem, and the differences are seen mostly from the hardness perspective. LMD-HH is a promising tool material to reduce wear in hot stamping dies.

Design of a Test Rig for the Characterization of Thermal Fatigue and Soldering Resistance of the Surfaces of Tool Steels for High‐Pressure Die‐Casting Dies

Development of Estimation Procedure of Contact Heat Transfer Coefficient at the Part–Tool Interface in Hot Stamping Process

Structural Features of Fatigue Crack Propagation of a Forging Die Made of Chromium-Molybdenum-Vanadium Tool Steel on Its Durability

A New High Temperature Test Rig for Corrosion-wear in Molten Metal and Its Application

Fatigue and ratcheting assessment of AISI H11 at 500°C using constitutive theory coupled with damage rule

Alloying Design and High-temperature Wear Property of Cast Hot-forging Die Steel

Dissipative and thermal aspects in cyclic loading of additive manufactured AISI 316L

Experimental and Numerical Study on Friction and Wear Performance of Hot Extrusion Die Materials

3D characterization and modeling of low cycle fatigue damage mechanisms at high temperature in a cast aluminum alloy

Effect of Temperature on Deformation and Fatigue Behaviour of A356–T7 Cast Aluminium Alloys Used in High Specific Power IC Engine Cylinder Heads

Casting Design Optimization Using Numerical Simulation of Precision Forging Die for Large Titanium Alloy Integral Bulkhead

Application of a 3D-Printed Part with Conformal Cooling in High-Pressure Die Casting Mould and Evaluation of Stress State During Exploitation

Thermal Distortion Testing at Ferrous Superheat Temperatures

Research on Thermal Performances of the Cast Hot-working Die Steel with High Wear Resistance

Laboratory Testing to Characterize the Use of PVD Coatings and Alternate Die Materials for Reducing Soldering and Erosion for Aluminum Die Casting Applications

Tribological Behavior of Laser Textured Hot Stamping Dies

High temperature friction and wear of hot stamping tool materials produced by laser metal deposition

Microstructure and Mechanical Properties of Hot Forging Die Manufactured by Bimetal-Layer Surfacing Technology

Optimizing the Morphology of Primary Carbides and Mechanical Properties during Processing Of Cast-Steel (Din Gx210crv12 1) Press-Forming Dies

A Case Study for a Worn Tool Steel in the Hot Stamping Process