Abstract:In the process of hot-dip galvanizing, some beneficial alloying elements are deliberately added to the molten Zn bath, in order to improve the coating properties, such as formability and corrosion resistance. Sb is one of the interesting alloying additions to the Zn bath, as it can decrease the viscosity and the surface tension of the molten Zn, contributing to producing a uniform Zn coating. Due to the low solid solubility of Sb in molten Zn at galvanising temperature, Sb-rich intermetallic particles were always found in the galvanized layers. The presence of Sb-rich phases may affect the structural properties and corrosion performance of galvanized coating. In the literature, it was reported that small addition of Sb has no significant effect on the structure and growth of galvanized layers, but a higher amount (>1%, mass fraction) of Sb can promote the dendritic solidification of Zn. In order to understand the mechanism of Sb addition on the structure and growth of galvanized coating, it is essential to identify the crystal structure of Sb-rich phases. It was reported that the Sb-rich phases found in the eta layer of a galvanized coating corresponds to the electron diffraction patterns of Sb2Zn3. However, some researchers hold that the Sb2Zn3 compound does not exist at room temperature, since it can transform to Sb3Zn4 and Zn at some elevated temperature. Consequently, in this work, the structure of Sb-rich intermetallic phase in theZn-1.2Sb (1.2%Sb) alloy has been investigated by SEM and TEM. SEM/EDS showed that Sb is present in the form of Sb-rich intermatallic phase and there is no detectable Sb in the Zn solid solution. Transmission electron diffractions analysis and EDS results indicated that the composition of Sb-rich intermatallic phases is close to that of Sb2Zn3, whereas the structure is totally different from the latter. The corrosion resistance of Zn-1.2Sb alloy has been analysed by electrochemcial polarization measurements in the different solutions. The analysed results showed that the Sb-rich phase has no obvious effect on the oxygen reduction reaction, in the aerated 0.1 mol/L NaCl (pH=6.5) solution. However, the Sb-rich phase can promote the hydrogen evolution reaction, in the deaerated acidic solution (0.1 mol/L NaCl, pH=3). Corrosion pits were found in the Zn matrix around the Sb-rich phases by SEM observations, which indicate that Zn has higher activity than Zn-Sb phase.

Effect of Sb on the Corrosion Behavior of Low-Alloy Steels in a Simulated Polluted Marine Atmosphere

Corrosion and SCC Initiation Behavior of Low-Alloy High-Strength Steels Microalloyed with Nb and Sb in a Simulated Polluted Marine Atmosphere

Integral effects of Ca and Sb on the corrosion resistance for the high strength low alloy steel in the tropical marine environment

Research on the Chloride Ion Corrosion Resistance of Cu-Sb-Added Low-Carbon Steel

Corrosion Behaviour of Pb-0.05%Sb Alloy and Pb in Boiling H2SO4 Aqueous Solution

Effects of Sb on corrosion behavior of Mg-6Al alloy

Effect of SO2 pollution on corrosion behavior of Q235B steel in hot and humid marine atmosphere

Investigation of Microstructure and Corrosion Behavior of Weathering Steel in Aqueous Solution Containing Different Anions for Simulating Service Environments

The Effect of Sulfide on the Corrosion Behavior of Carbon Steel in Natural Waters

Field corrosion study of 690 MPa grade Sb-containing high strength bridge steel in tropical oceanic environment

Effect of Sb-Rich Intermetallic Phase on the CorrosionResistance of Zn Alloy in Near-Neutral and Acidic Solutions

The Effect of B and Sb on the Corrosion Behavior of T6-treated Al-Si-Mg Alloys

Effect of Al alloying on corrosion performance of steel

INFLUENCE OF SULFATE REDUCING BACTERIA ON CORROSION BEHAVIOR OF HSn70-1A ALLOY

Effects of Cu and Sb on Corrosion Resistance of ZA27 Alloy

Effect of One Sulfate-Reducing Bacterium SRB-Z Isolated from Pearl River on the Corrosion Behavior of Q235 Carbon Steel

EFFECT OF Sb AND Mn ADDITIONS ON THE CORROSION BEHAVIOUR OF Zn

Synergistic Effect of Microalloying Elements on the Corrosion Behavior of an Industrially Produced Low-Carbon Steel

The influence of sulphate‐reducing bacteria on heterogeneous electrochemical corrosion behavior of Q235 carbon steel in seawater

Corrosion Behavior of Q235 Steel in Atmospheres Containing SO2 and NaCl

Effect of Tin on the Corrosion Behavior of Sea-Water Corrosion-Resisting Steel