Synergistic Effect of Microalloying Elements on the Corrosion Behavior of an Industrially Produced Low-Carbon Steel
Hailin Xiao,Tao Sun,Kai Lei,Zhao Luo,Zhong Xi,Xintong Lian,Han Dong
DOI: https://doi.org/10.1007/s12540-024-01853-z
IF: 3.451
2024-11-28
Metals and Materials International
Abstract:This study comparatively investigates the synergistic effects of rare earth elements (La and Ce) and microalloying elements (C, Cu, P, Cr and Sb) on the corrosion behaviors of an industrially produced low-carbon steel in a simulated industrial atmospheric environment through dry-wet immersion testing and electrochemical testing. The experimental results show that the corrosion rate of Q355 steel significantly decreases after microalloying. The addition of rare earth (RE) elements modifies harmful inclusions to reduce the tendency for pitting corrosion. Additionally, the segregation of RE at the matrix-rust layer interface enhances the bond between them, thus improving the stability of the rust layer. The incorporation of RE and Sb notably promotes the formation of a stable and continuous α-FeOOH phase in the rust layer to enhance its compactness. Moreover, the enrichment of Sb in the inner rust layer effectively prevents corrosive S ions from infiltrating the substrate. Alloying elements facilitate the enrichment of Sb in the inner rust layer. The interaction of Cu, Cr, P, and Sb elements promotes the formation of dense and stable phases in the rust layer, which further improves the corrosion resistance properties of Q355 steel.
materials science, multidisciplinary,metallurgy & metallurgical engineering