Abstract:The fatigue behavior of as-cast Mg–12%Zn–1.2%Y–0.4%Zr alloy has been investigated. The S–N curve showed that the fatigue strength at 107 cycles was 45MPa. Scanning electron microscopy observations on the surfaces of the failed and unfailed specimens (after up to 1×107 cycles) suggested that the slip bands could act as preferential sites for non-propagating fatigue crack initiation, and the I-phase could effectively retard fatigue crack propagation (FCP). The macro fracture morphology clearly indicated that the overall fracture surface was composed of three regions, i.e. a fatigue crack initiation region (Region 1), a steady crack propagation region (Region 2) and a tearing region (Region 3). High-magnification fractographs showed that only porosities can act as the crack initiation sites for all specimens. Moreover, for specimens with fatigue lifetimes lower than 2×105 cycles, the cracks mostly initiated at the subsurface or surface of the specimen. However, when the fatigue lifetime was equal to or higher than 2×105 cycles, the fatigue crack initiation sites transferred to the interior of the specimen. The maximum stress intensity factors corresponding to the transition sites between Regions 1, 2 and 3 were 2 and 4.2MPam1/2, respectively. When the maximum stress intensity factor Kmax was lower than 4.2MPam1/2, in the steady crack propagation region, due to the retarding effect of I-phase/α-Mg matrix interfaces, the fatigue cracks tended to pass the I-phase/α-Mg matrix eutectic pockets directly and propagated through the grain cells, resulting in the formation of many flat facets on the fracture surface. However, when the maximum stress intensity factor was higher than 4.2MPam1/2, in the sudden failure region, the rigid bonding of I-phase/α-Mg matrix interfaces was destroyed and the cracks preferentially propagated along the interfaces, which resulted in the fracture surface being almost completely composed of cracked I-phase/α-Mg matrix eutectic pockets. Based on microstructural observation and the fracture characteristics of the two regions, it is suggested that with an increase in crack tip driving force, the FCP mode changes from transgranular propagation to intergranular propagation.

Effects of phase difference and stress ratio on biaxial tension–tension fatigue crack propagation behavior of rolled ZK60 magnesium alloy

Fracture parameters analysis of compact tension specimens with deflected fatigue cracks: ZK60 magnesium alloy

The Fatigue Behavior of I-phase Containing As-Cast Mg–Zn–Y–Zr Alloy

Influence of Microstructure on Tensile Properties and Fatigue Crack Growth in Extruded Magnesium Alloy AM60

The Micro-Mechanism of Fatigue Crack Propagation for a Forged Mg–Zn–Y–Zr Alloy in the Gigacycle Fatigue Regime

Effects of orientation on the fatigue crack growth behaviors of the ZK60 magnesium alloy in air and PBS

Flow and fracture study for ZK60 alloy at dynamic strain rates and different loading states

Influences of stress states and loading directions on the anisotropic fracture of magnesium alloy AZ31B sheet under tension-dominated forming conditions

Analyses of the fatigue crack propagation process and stress ratio effects using the two parameter method

Effects of Distance and Alignment Holes on Fatigue Crack Behaviors of Cast Magnesium Alloys

Effects of the transverse stress on biaxial fatigue crack growth predicted by plasticity-corrected stress intensity factor

The Effect of Microstructure on the Plastic Strain Localization and Fatigue Crack Initiation in Cast Mg–8Gd–3Y–0.5Zr Alloy

Mechanical Behavior and Microstructure Evolution of a Rolled Magnesium Alloy AZ31B under Low Stress Triaxiality

Quantitative assessment of the microstructural factors controlling the fatigue crack initiation mechanisms in AZ31 Mg alloy

The Small Fatigue Crack Growth Behavior of an AM60 Magnesium Alloy

Effects of Biaxial Mean Stress on the Critical Plane Orientation under Biaxial Tension/compression Fatigue Loading Conditions

Stress-state dependency of ductile fracture in an extruded magnesium alloy and its underlying mechanisms

Quantitative analysis of the deformation modes and cracking modes during low-cycle fatigue of a rolled AZ31B magnesium alloy: The influence of texture

Effect of stress ratio on fatigue-crack growth in 7075-T6 aluminum-alloy sheet

Effect of Microstructure on Small Fatigue Crack Initiation and Early Propagation Behavior in Mg-10Gd-3Y-0.3Zr Alloy

Effect of loading conditions on short fatigue crack propagation behaviours in cast Al Si alloys