Mechanical performance and radar-absorption capacity of carbon Material–Reinforced polymethacrylimide foam: Preparation, comparison, and design
Shijun Song,Chao Xiong,Junhui Yin,Zhaoshu Yang,Aijun Gao,Fang Zhao,Yang Cao,Chao Han,Junjie Xie,Bo Tang,Lei Liu
DOI: https://doi.org/10.1016/j.compositesb.2024.111317
IF: 11.322
2024-02-20
Composites Part B Engineering
Abstract:Herein, radar-absorbing polymethacrylimide (RAPMI) foam was prepared using the particle foaming method. Nineteen samples were prepared based on different ratios and absorbent types, and their microstructural characteristics were analyzed and compared. Their dielectric constant and loss tangent were measured at 2–18 GHz, and the electromagnetic (EM) characteristics were analyzed. Subsequently, their mechanical properties were tested. The effect mechanism of the absorbents on the EM and mechanical behavior was analyzed, and the experimental data were compared. Finally, a laminated foam was designed. Results show that the samples can achieve 90% bandwidth effective absorption (reflection loss ≤ −10 dB) at 33.6-mm thickness and 18.6%, 32.4%, 62.5%, 62.9%, 35.7%, and 51.9% maximum increases in compressive strength, compressive modulus, tensile strength, tensile modulus, shear strength, and shear modulus, respectively, compared with particle polymethacrylimide (PMI) foam. The designed laminated foam can theoretically achieve full-band effective absorption at a minimum thickness of 15.3 mm. The preparation of RAPMI foam is simple and inexpensive, and this research strengthens the engineering application of PMI foam in cutting-edge fields, such as military and aerospace. It provides an important reference for researchers, technicians, and engineers in the fields of absorbing materials, polymers, and composites.
engineering, multidisciplinary,materials science, composites