Abstract:Many components in secondary side of pressurized water reactors (PWRs) are made of carbon steels and low alloy steels. The corrosion products produced by the flow accelerated corrosion (FAC) of these components can deposite on the surface of steam generator (SG) tubes and decrease the heat transfer efficiency of SG tubes. Moreover, the enrichment of foreign ions (e.g. Cl- and Pb2+) occurs with the sedimentation of corrosion products and causes the local environment degradation, and thus accelerates the failure of SG tubes. In order to decrease the FAC of carbon steels and low alloy steels, pH controllers are often added to adjust the pH value of secondary water. The water chemistry environment of secondary side in PWRs has experienced various treatment techniques, such as phosphate treatment, all volatile treatment (AVT), morpholine (MPH) treatment, ethanolamine (ETA) treatment, and boric acid treatment. In comparision with AVT, ETA can significantly reduce the concentration of Fe in the steam-water phase region and water supply system because of its higher alkalinity and lower molar concentration in feedwater. Due to the high resistance to corrosion and stress corrosion cracking in high temperature and high pressure water, alloy 800 is often used as steam generator tubes in nuclear power plants and thus becomes increasingly attractive among researchers. However, few studies focus on the effect of ETA on the corrosion behavior of alloy 800 in high temperature and high pressure water. This work mainly aims to investigate the corrosion behavior of alloy 800 in NaOH and ETA solutions at 300 degrees C by potentiodynamic polarization curve, electro-chemical impedance spectra (EIS), SEM and XPS. The electrochemical results demonstrate that the addition of ETA decreases the current density of anodic and cathodic reactions, and increases the corrosion potential of alloy 800. Besides, ETA addition significantly increases the resistance of inner oxide layer and makes the oxide film more compact, which increases the film resistance of alloy 800 in high temperature water. Through the morphology observation and composition analysis, it is found that ETA addition can promote the formation of Cr-rich layer and increase the ratio of chromium in the oxide films although the deposition of magnetite is enhanced on the surface of alloy 800. For stainless steels and nickel-based alloys in high temperature water, the Cr-rich oxide layer can inhibit the diffusion process of 0 and metal ions, and reduces the corrosion rates of alloys. Therefore, the corrosion resistance of alloy 800 is enhanced after ETA is added in high temperature water.

Corrosion rate of low carbon steel in simulated feed water for heat exchanger in ammonia plant

Corrosion resistance comparison of various carbon steel in inlet water of heat exchanger’s Kujang ammonia plant

Corrosion Rate Analysis of Steam Boiler Superheater

Corrosion Of Carbon Steel In Typical Water Environments Of Thermal Power Plant

Corrosion Behavior of 16mnr Steel and Welded Joints in High-Temperature Naphthenic Acid

Corrosion resistance characteristics of different metal materials in flue gas of rolling steel heating furnace

Corrosion Investigation of Commercially Available Linepipe Steel in CO2 Environment

Corrosion of Carbon Steel in Oxygen and NaCl Concentration Cells: the Influence of Solution Temperature and Aeration

The Effect of Ultrasonic Waves on the Rate of Corrosion in Low Carbon Steel with Hydrochloric Acid Solution

Corrosion Behavior of Alloy 800 in Naoh and Eta Solutions at 300 Degrees C

Comparative Study on the Corrosion Behavior of Materials in Heat Recovery Steam Generators for Combined Cycle Power Plant, Based on Sulfuric Acid Concentrations: Carbon Steels vs. Duplex Stainless Steel (UNS S32205)

Corrosion failure analysis of the heat exchanger in a hot water heating boiler

Corrosion Behavior of Superalloys in High Temperature Gas Cooled Reactor in Impure Helium with Corrosion Time

Corrosion Behavior of Carbon Steel at Typical Positions of an Amine-Based CO2 Capture Pilot Plant

A Study on the Corrosion Behavior of Carbon Steel Exposed to a H2S-Containing NH4Cl Medium

Corrosion Characteristics of Electroless Ni–P Coating in Dichloropropanol (DCP) Solution

Corrosivity of water for concrete and metal water resources infrastructure with modification of the DIN Method and Langelier Saturation Index of Metcalf and Eddy

High Temperature Corrosion Resistance of Different Commercial Alloys Under Various Corrosive Environments

Corrosion Performance of Carbon/stainless Steel in Amine‐based Solvents under Different Conditions for CO2 Chemical Absorption Process

Study on the Influences of Ammonia Nitrogen in Reclaimed Water on the Circulating Cooling Water System of Power Plants

Molecular dynamics simulation of corrosion and its inhibition: comparison of structural stability of Fe/FeNi/FeNiCr/FeNiCrTi steels under high-temperature liquid lead