Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

Corrosion Electrochemical Behavior of 20 Steel and 16Mn Steel in Simulated CO2 Flooding Environment

Corrosion Behaviors of 25crmnva Steel in CO2 Flooding Enhanced Oil Recovery System

Corrosion Behavior of High-Strength Steel for Flexible Riser Exposed to CO 2 -Saturated Saline Solution and CO 2 -Saturated Vapor Environments

Corrosion Behavior of Oxide Scale of 5cr Steel in CO2 Flooding Environment

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

Study on Under-Deposit Corrosion Behavior of X65 Steel in Simulated CO2 Saturated Produced Water

Corrosion Behaviour of N80 Carbon Steel in Formation Water under Dynamic Supercritical CO 2 Condition

Corrosion Behavior of X65 Carbon Steel in Simulated Oilfield Produced Water

Electrochemical Behavior and Corrosion Products of Casing Steel under CO2 Condition

Corrosion Behavior of Carbon Steel Pipelines under Different Deposits in Oil and Gas Transportation

Corrosion Behavior of Pipeline Steel Welds in Simulated Produced Water with Different Co2 Partial Pressures under High Temperature

Corrosion Behavior of N80 Steel in CO2-saturated Formation Water

Electrochemical Corrosion Behavior of 16mn Steel in Simulated Oil-Field Aqueous Medium

Corrosion Behavior of Low-Alloy Steel with Martensite/Ferrite Microstructure at Vapor-Saturated Co2 and Co2-Saturated Brine Conditions

Electrochemical corrosion behavior of carbon steel under dynamic high pressure H 2S/CO 2 environment

Localized corrosion of carbon steel in a CO2-saturated oilfield formation water

Corrosion Behavior of Low‐alloy Steel Used for Pipeline at Vapor‐saturated CO2 and CO2‐saturated Brine Conditions

Corrosion Behavior of X65 Steel in CO2-saturated Oil/water Environment of Gathering and Transportation Pipeline

Effect of temperature on electrochemical corrosion behavior of N80 and KO80SS steels in the stratum water with saturated CO2

Investigation of the Electrochemical Behavior of CO2 Corrosion Product Scale of X65 Steel

Corrosion Behavior of Gathering Pipeline Steel in the CO2/Oil/Water Corrosive Environment