Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

Effect of CO2 content on corrosion non-uniformity of 20# steel in oil–water two-phase based on wire beam electrode technique

Experimental study on corrosion of 20# steel in oil-water stratified liquids based on wire beam electrode technique

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

Factors Influencing the CO2 Corrosion Pattern of Oil–Water Mixed Transmission Pipeline during High Water Content Period

Corrosion Electrochemical Behavior of 20 Steel and 16Mn Steel in Simulated CO2 Flooding Environment

A comprehensive study on the effect of rock corrosion and CO2 on oil-water interfacial tension during CO2 injection in heavy oil reservoirs

Corrosive Experimental Study on Simulating Produced Water of the Oil-gas Field

Effect of High-Concentration O2on Corrosion Behavior of X70 Steel in Water-Containing Supercritical CO2with SO2

Study on corrosion properties of pipelines in simulated produced water saturated with supercritical CO2

Study on the Corrosion Mechanism of N80 Steel in Simulated Oxygen-Reduced Air Drive Production Wellbores

Corrosion Inhibition Properties of Corrosion Inhibitors to under-Deposit Corrosion of X65 Steel in CO2 Corrosion Conditions

Effect of H2O Content on the Corrosion Behavior of X52 Steel in Supercritical CO2 Streams Containing O2, H2S, SO2 and NO2 Impurities

Effect of CO2 Partial Pressure on the Corrosion Behavior of J55 Carbon Steel in 30% Crude Oil/Brine Mixture

Corrosion Behavior of J55 and N80 Carbon Steels in Simulated Formation Water under Different CO2 Partial Pressures

Corrosion behaviour of X80 pipeline steel welded joint in H2O- saturated supercritical-CO2 environment

Effects of Pipeline Corrosion on the Injection Water Quality of Low Permeability in Oilfield

Effect of impurities on the corrosion behavior of CO2 transmission pipeline steel in supercritical CO2-water environments

Electrochemical Investigation of the Corrosion of Different Microstructural Phases of X65 Pipeline Steel under Saturated Carbon Dioxide Conditions

Corrosion behavior of X70 steel in the supercritical CO2 mixed with SO2 and saturated water

CO2 corrosion behavior of simulated heat-affected zones for X80 pipeline steel