A Characterization Study on Toughening Vinyl Ester Composites Using Annealed Vinyl Silane Functionalized Biosilica from Foxtail Millet Husk and Nettle Fibre
R. Jamuna,Sumanth Ratna Kandavalli,Praveen Kumar Balguri,Pothamsetty Kasi V. Rao
DOI: https://doi.org/10.1007/s12649-024-02790-z
2024-11-07
Waste and Biomass Valorization
Abstract:This study effectively demonstrated the ability of nettle fiber, along with annealed, vinyl silane-functionalized foxtail millet husk biosilica, to enhance the mechanical and wear properties of vinyl ester composites. Vinyl ester resin, known for its toughness, corrosion resistance, and high elongation, was used as the matrix material, combined with nettle fiber and biosilica to develop the composite. The biosilica was meticulously extracted from foxtail millet husk, followed by annealing at 1200 °C for 2 to 4 h, and a vinyl-silane surface modification to improve interfacial bonding. The composite fabrication employed a hand lay-up process, ensuring proper impregnation of the fibers and uniform distribution of the biosilica.The mechanical properties of the composites were significantly enhanced, with specimen D12 exhibiting the best performance. It achieved a tensile strength of 147 MPa, a flexural strength of 167 MPa, a compressive strength of 157 MPa, and a V-Notch shear strength of 21.3 MPa. These values represent substantial improvements over the baseline specimen A, which recorded 51 MPa tensile strength, 64 MPa flexural strength, 58 MPa compressive strength, and 11.4 MPa V-Notch shear strength. On the other hand, specimen E12 demonstrated superior wear properties, achieving the lowest specific wear rate of 0.00081 mm3/Nm and a coefficient of friction (COF) of 0.085. This represents a significant enhancement compared to the baseline specimen A, which showed a specific wear rate of 0.0198 mm3/Nm and a COF of 0.55.The SEM analysis provided key insights into the microstructure of the composites. It revealed that while uniform dispersion of biosilica particles (as seen in some specimens) contributed to the improved structural integrity and mechanical performance, the agglomeration of biosilica particles in other specimens created weak points that could act as stress concentrators, potentially leading to premature failure. Overall, this study highlights the critical role of material composition and processing techniques in developing high-performance vinyl ester composites with enhanced mechanical strength, wear resistance, and durability.
environmental sciences