Abstract:The microstructural characteristics and morphological attributes of the target material, along with its intrinsic properties, can significantly influence the performance of the resultant film. Currently, commercially available nickel-vanadium targets employed in the industry have not been subjected to investigations aimed at controlling grain size and grain orientation. This study examines the effects of unidirectional rolling at room temperature, combined with substantial deformation, on the alterations in microstructure, texture evolution, and mechanical properties of the NiV7 alloy. The process of severe plastic cold rolling leads to a continuous elongation and refinement of the grains. The changes in microstructure and texture of the cold-rolled sheets were analyzed using electron backscatter diffraction (EBSD) technology. At an 80% reduction, a significant number of sub-grains are observed, which transform into deformed grains as the reduction reaches 95%. With a thickness reduction of 96.6%, the average grain size is approximately 1.10μm. Further increases in reduction do not lead to significant alterations in the grain structure; instead, the grain orientation progressively becomes more uniform with higher levels of deformation. The combination of substantial deformation and lower rolling rates results in an increased number of high-angle grain boundaries. The alloy displays various textures throughout the rolling process, including S-type, copper-type, brass-type, fiber, and cubic textures. Notably, the prevalence of S-type and fiber textures diminishes as the degree of deformation increases, while the cubic texture becomes increasingly prominent. Upon achieving a reduction of 95%, the cubic texture emerges as the dominant texture. A transmission electron microscope (TEM) was utilized to examine the extensive array of dislocations, dislocation cells, dislocation walls, and shear bands generated during the cold rolling process. At a deformation level of 96.6%, the ultimate tensile strength of the alloy demonstrates a significant enhancement, attributed to mechanisms of dislocation strengthening and grain strengthening, reaching a value of 1231±20 MPa, accompanied by a post-fracture elongation of approximately 2%. The ultimate tensile strength exhibited an increase of 781±20 MPa compared to the sample prior to the rolling process; however, there was a notable reduction in plasticity.

The effect of cold rolling degree on microstructure, crystallographic texture and mechanical properties of Haynes® 282® wrought nickel superalloy

Aging behavior of Haynes 282 wrought nickel superalloy subjected to a cold pre-deformation by differential speed rolling

Effect of Post Processing Heat Treatment Routes on Microstructure and Mechanical Property Evolution of Haynes 282 Ni-Based Superalloy Fabricated with Selective Laser Melting (SLM)

Effect of Cold Rolling and Cryogenic Treatment on the Microstructure and Mechanical Properties of Fe–32Ni Alloy

Effect of Cold Rolling on the Microstructure and Mechanical Behaviors of High-Nitrogen and Low-Nickel Alloy

Effect of Post-Deformation Heat Treatment on the Microstructure and Properties of Inconel 617 Alloy

Optimizing Tensile Properties and Hardness of Inconel 718 by Cold Rolling

Effects of cold rolling and annealing treatment on microstructure and properties of CoFeNiMnV high‐entropy alloys

Studying the Effect of Cold Rolling and Heat Treatment on the Microstructure and Mechanical Properties of the Fe36Mn20Ni20Cr16Al5Si3 High Entropy Alloy

Effect of cold rolling on aging precipitation behavior and mechanical properties of Cu–15Ni–8Sn alloy

Effect of Cold Rolling on Texture and Microstructure Development in Annealed Incoloy 800 Fabricated Using Selective Laser Melting

Recrystallization behavior and mechanical properties of Haynes 282 fabricated by wire-arc additive manufacturing with post-heat treatment

Severe plastic cold rolling effects in Nickel-Vanadium alloy: Microstructure, texture evolution and mechanical properties

Effects of Annealing on Microstructure and Mechanical Properties of Nano-Grained Ni-Based Alloy Produced by Severe Cold Rolling

Comparative analysis of cold and warm rolling on tensile properties and microstructure of additive manufactured Inconel 718

The Effects of Microstructure and Microtexture Generated During Solidification on Deformation Micromechanism in IN713C Nickel-Based Superalloy

Effect of cross cold rolling and annealing on microstructure and texture in pure nickel

Microstructure and Properties of Bulk Al0.5CoCrFeNi High-Entropy Alloy by Cold Rolling and Subsequent Annealing

Hot Tensile Behavior of Cold-Rolled Inconel 718 Alloy at 650 °C: the Role of Δ Phase

Microstructure evolution dependence of work-hardening characteristic in cold deformation of a difficult-to-deform nickel-based superalloy

Effect of heat treatment on the microstructure and mechanical properties of cryogenic rolling 2195 Al–Cu–Li alloy