Abstract:Fabricating biobased heat-resistant photoactive acrylates from aliphatic biomass for three-dimensional (3D) printing is a great challenge with enormous implications for energy saving and sustainable development of polymers. Herein, two fully biobased acrylate monomers with di- or tri-functionality (BHMP2 and BHMP3) are synthesized from renewable glycidyl methacrylate and succinic acid or itaconic acid through a one-step method under solvent-free condition. These monomers are then cured by digital light processing 3D printing without diluters. The influences of structure on the curing behavior and performances are systematically studied. The BHMP3 resin shows excellent thermal and mechanical properties. Specifically, its glass transition temperature and heat deflection temperature under 0.455 MPa reach up to 183 and over 250 °C, respectively, while its tensile strength, modulus, and hardness are as high as 45.2 MPa, 4480 MPa, and 0.49 GPa, respectively. The outstanding performances of BHMP3 resin result from its compact cross-linking structures. This work pioneers a sustainable way to produce heat-resistant photoactive acrylates from renewable low-cost aliphatic biomass for photocurable 3D printing.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acssuschemeng.0c02168.1H NMR of BHMP2 and BHMP3, HRMS of BHMP2 and BHMP3, FTIR spectra of BHMP2 and BHMP3 resins before and after UV curing, PALS spectra of BHMP2 and BHMP3 resins, pictures of 3D objects printed by BHMP3 resin with 100 g weight on it after insulation at 250 °C for 1 h and 3D objects printed by BHMP3 resin with 1000 g weight on it after insulation at 180 °C for 1 h, pictures of 3D objects printed by BHMP2 resin with 100 g or 1000 g weight on it broke down after heating in an oven, and a comparison of bio-degree and Tg of biobased and petroleum-based acrylates for 3D printing in the literature (PDF)This article has not yet been cited by other publications.

Three-Dimensional Printing Fully Biobased Heat-Resistant Photoactive Acrylates from Aliphatic Biomass