Obtained Large Room-Temperature TCR of La0.67Ca0.25Sr0.08MnO3 Ceramics by Optimizing Sintering Temperature
Zihao Chen,Jiamei Han,Jiabin Jiang,Xiaolu Liang,Haitao Wang,Yao Wang,Zhenyu Wang,Zimeng Pan,Jiankun Sun,Jun Ma,Xuexing Jiang,Jubo Peng,Xin Gu,Xiang Liu
DOI: https://doi.org/10.1016/j.ceramint.2024.06.275
IF: 5.532
2024-01-01
Ceramics International
Abstract:Over the past few decades, perovskite manganese oxide La-x(CaSr)(1-x)MnO3 has presented new opportunities for uncooled infrared bolometers due to its exceptional electrical transport performance. In this study, La0.67Ca0.25Sr0.08MnO3 (LCSMO) ceramics were prepared at different sintering temperatures (T-s, T-s = 1450, 1470, 1490, 1510, 1530 degrees C) by changing the previous sol-gel preparation process parameters. The research results indicated that the tolerance factor (tau) of the ceramics is tau = 0.935, and all ceramics exhibit a Pnma space group perovskite structure with excellent crystallinity. LCSMO ceramics exhibit good crystal quality and higher room-temperature TCR (14.58 % K-1) at T-s = 1510 degrees C. As T-s increases, the grain size, Mn-O bond length (d(Mn-O)), Mn-O-Mn bond angle (theta(Mn-O-M)n) and cell volume (V) of ceramics have a slight affected. The decrease of grain boundary scattering, electron-electron scattering, and strong coupling between electrons, so the peak resistivity value of all sintered samples firstly decreases and then increases with the increase in T-s, which effectively yields ceramics with high TCR. The peak TCR value (TCRmax) increased from 8.38 % K-1 (T-s = 1450 degrees C) at 296.91 K to 14.58 % K-1 (T-s = 1510 degrees C) at 298.18 K. On the same component, the TCRmax was increased by 42 % from 8.38 % K-1 to 14.58 % K-1 at T-s = 1450 degrees C-1510 degrees C. The high room-temperature TCR of LCSMO is expected to be used in advanced uncooled infrared bolometers, providing a basis for studying the influence of Ts on the electrical transport performance of ceramics.