Thermoelectric properties and microstructure of perovskite layer La2 xSrxCoO4

H Suzuki,JF Li,R Watanabe

2001-01-01

Abstract:The perovskite-type La1-ySryCoO3 is known to exhibit conduction mechanism transition from semiconductive to semi-metallic conduction below 773K. As a result it is difficult to increase ZT value for this composition. No such conduction transition is observed in the perovskite-layer La2-xSrxCoO4 composition, which shows small polalon hopping mechanism in a wide temperature range. Therefore,, high ZT value may be obtainable in this La2-xSrxCoO4 system. In the present study, La2-xSrxCoO4 (X=1.0, 1.1 and 1.2) and La1-ySryCoO3 (y==0.0, 0.1 and 0.2) were prepared by a solid reaction method. The Seebeck coefficient and electrical conductivity were measured and analyzed. The phase's qualitative analysis and microstructure were analyzed by SEM and X-ray diffraction. It has been found that, La2-xSrxCoO4 exhibits high Seebeck coefficient than La1-ySryCoO3, but its electrical conductivity is 2-4 orders lower than that of La0.9Sr0.1CoO3 up to 500K in He atmosphere However, the increase ratio of power factor on in the La2-xSrxCoO4 systems is greater than the La2-ySryCoO3 systems up to 500K, indicating that the conduction mechanism of the La2-xSrxCoO4 systems may remains as semiconductive up to high temperature. La2-xSrxCoO4 and La1-xSrxCoO3 show plate-like and isoaxial microstructures, respectively. Incidentally the relative densities of La2-xSrxCoO4 (x=1.0, 1.1 and 1.2) sintered at 1573K and La1-ySryCoO3 (y=0.0, 0.1 and 0.2) sintered at 1673K were about 98%.