Preparation and Electrical Transport Property of LaxSr1-xTiO3 Oxide Thermoelectric Materials

Shang Pengpeng,Zhang Boping,Li Jingfeng,Zhao Lidong,Liu Weishu,Ma Ning

DOI: https://doi.org/10.3321/j.issn:1002-185X.2009.z2.085

2009-01-01

Rare Metal Materials and Engineering

Abstract:The single phase perovskite LaxSr1-xTiO3 (0 <= x <= 0.15) ceramics were prepared by sol-gel process and spark plasma sintering (SPS). The thermal treating conditions were selected out through TG-DTA analysis of the drying gel. The phase structures of ceramics were studied with X-ray diffraction (XRD). The size and distribution of grains were tested by scanning electron microscopy (SEM). Sintering temperature of the as-prepared samples was significantly decreased compared with conventional solid-state reactions. Seebeck coefficient and electrical conductivity were measured from room temperature to 679 K. The optimal lanthanum doping content x was 0.08 mol, with which the La0.08Sr0.92TiO3 sample shows the maximum power factor (PF) of 2.95 mu W.m(-1).K-2 at 679 K. The larger PF would be obtained at higher measuring temperature.