Abstract:Since the period required for testing the atmospheric corrosion of steel is long, most studies have focused on the corrosion behavior in less than three years, making exploring long-term atmospheric corrosion particularly valuable. This study investigates the corrosion behaviors, corrosion models, and mechanical properties of Q235 welded steel pipes collapsing due to corrosion after 25-year service in an urban industrial atmospheric environment using SEM, XRD, electrochemical methods, 3-D noncontact surface profilometry, and static tensile testing. The typical morphologies of & alpha;-FeOOH, & gamma;-FeOOH, and Fe3O4 and the effect of the content of various corrosive materials on the corrosion rate of the steel pipes are identified and analyzed. Then, the influence of different corrosion degrees on the mechanical properties of the steel pipes is examined by considering the morphologies of the rust pits. The results show that the wetting-drying cycles affect the structures of the rust layers and their protective properties. The rust layers on the sheltered surface are thicker but less protective than those on the exposed surface. In the wet state, FeSO4 accelerates ion transfer, while Fe3O4 facilitates electron transfer. These processes collectively contribute to the corrosion of Q235 steel. Moreover, as the time-of-wetness of the rust layers on sheltered specimens increases, the corrosion rate of Q235 steel also accelerates. The corrosion model combines pitting and uniform corrosion and gradually changes from predominated by pitting to thickness as the corrosion degree increases. The corrosion morphology impacts the mechanical properties of the welded steel pipes, and the influences of the thickness loss and maximum rust pit depth on these properties are profound.

Research on Corrosion Causes of Common Metal Material in Power Grid

Corrosion-Fatigue Analysis of Wires in Bridge Cables Considering Time-Dependent Electrochemical Corrosion Process

Corrosion Behaviors and Mechanical Properties of Q235 Steel Pipes Collapsing Due to Corrosion after 25-Year Service in Urban Industrial Atmospheric Environment

Corrosion Failure Analysis of Fittings Used for Electrical Equipment in 220 kV Substation

Review on Soil Corrosion and Protection of Grounding Grids

Study on the Corrosion Characteristics of Grounding Materials in Acid Red Soil

Method for Calculating the Galvanic Corrosion Rate of Copper-steel Connected Ground Grids

Research Advances of Soil Corrosion of Grounding Grids

Influence of Air Pollution Factors on Corrosion of Metal Equipment in Transmission and Transformation Power Stations

Development status of Anti-corrosion Technology for Power Transmission Tower’s Steel Structure

The Effect of Atmospheric Chloride Ions on the Corrosion Fatigue of Metal Wire Clips in Power Grids

Analysis of Corrosion Causes of Ring Connection Fittings of ±800 kV Transmission Line

Corrosion evolution of electric power equipment metal materials under industrial pollution environment with high heat and high humidity

Transmission Structure Corrosion Due to Stray Currents and the Inspection and Mitigation Techniques: A Review

Research on Corrosion Problem and Residual Bearing Capacity of Transmission Tower Engineering Application Process

Corrosion Development of Carbon Steel Grids and Shear Connectors in Cracked Composite Beams Exposed to Wet-Dry Cycles in Chloride Environment.

Failure Analysis on Steel Structure Component for Outdoor Building of Substation

Influence of Current on Soil Corrosion of Galvanized Steel of Grounding Grids

Review of Corrosion Resistant Metals for Grounding

On-line Monitoring, Data Analysis for Electrolytic Corrosion of ±800 Kv High Voltage Direct Current Insulators

Fracture analysis of stainless steel universal joints in power grid equipment: A comparative study of cast and forged structures