Abstract:Since the period required for testing the atmospheric corrosion of steel is long, most studies have focused on the corrosion behavior in less than three years, making exploring long-term atmospheric corrosion particularly valuable. This study investigates the corrosion behaviors, corrosion models, and mechanical properties of Q235 welded steel pipes collapsing due to corrosion after 25-year service in an urban industrial atmospheric environment using SEM, XRD, electrochemical methods, 3-D noncontact surface profilometry, and static tensile testing. The typical morphologies of & alpha;-FeOOH, & gamma;-FeOOH, and Fe3O4 and the effect of the content of various corrosive materials on the corrosion rate of the steel pipes are identified and analyzed. Then, the influence of different corrosion degrees on the mechanical properties of the steel pipes is examined by considering the morphologies of the rust pits. The results show that the wetting-drying cycles affect the structures of the rust layers and their protective properties. The rust layers on the sheltered surface are thicker but less protective than those on the exposed surface. In the wet state, FeSO4 accelerates ion transfer, while Fe3O4 facilitates electron transfer. These processes collectively contribute to the corrosion of Q235 steel. Moreover, as the time-of-wetness of the rust layers on sheltered specimens increases, the corrosion rate of Q235 steel also accelerates. The corrosion model combines pitting and uniform corrosion and gradually changes from predominated by pitting to thickness as the corrosion degree increases. The corrosion morphology impacts the mechanical properties of the welded steel pipes, and the influences of the thickness loss and maximum rust pit depth on these properties are profound.

Influence of Air Pollution Factors on Corrosion of Metal Equipment in Transmission and Transformation Power Stations

Prediction and Assessment of Atmospheric Environmental Impact Based on Fumigation Dispersion Model——A Case Study of New Smelter at Xiangtan County

Corrosion Behaviors and Mechanical Properties of Q235 Steel Pipes Collapsing Due to Corrosion after 25-Year Service in Urban Industrial Atmospheric Environment

The Evolution of the Corrosion Mechanism of Structural Steel Exposed to the Urban Industrial Atmosphere for Seven Years

Research on Corrosion Causes of Common Metal Material in Power Grid

Corrosion evolution of electric power equipment metal materials under industrial pollution environment with high heat and high humidity

Corrosion of steel materials in four environmental conditions

Introduction to Atmospheric Corrosion Research in China

Corrosion Failure Analysis of Fittings Used for Electrical Equipment in 220 kV Substation

Corrosion Failure of Fittings in Electric Power Transmission Line in Typical Industrial Areas

Corrosion of Six Steel Materials in Typical Industry Atmosphere

Study on the influence law and mechanism of industrial atmospheric environment on the corrosion behavior of Q235 carbon steel

Review on Atmospheric Corrosion of Copper and Copper Alloys

Development status of Anti-corrosion Technology for Power Transmission Tower’s Steel Structure

CORROSION AND PROTECTION OF CONDENSERS IN XUZHOU POWER PLANT

EFFECT OF THE DIFFERENT PRE-RUSTED METHODS ON THE ATMOSPHERIC CORROSION BEHAVIOR OF CARBON STEEL

Investigation on Atmospheric Corrosion Behavior of Transmission Tower Materials in Simulated Industrial Environments

Long-term corrosion monitoring of carbon steels and environmental correlation analysis via the random forest method

Atmospheric Corrosion of Carbon Steels in Tropical and Subtropical Climates in Southern China

Prediction of Tempo-Spatial Patterns and Exceedance Probabilities of Atmospheric Corrosion of Q235 Carbon Steel Across China

Study on rust layers of carbon steel, weathering steel and alloy steel exposed to Shanghai atmosphere for three years