Abstract:The aim of this study is to improve the compressive strength of oil absorbent concrete (OAC) and to encourage its use in slope protection projects. This study used fly ash and slag produced in thermal power plants to substitute cement in significant amounts to prepare oil absorbent concrete (OAC). The water–cement ratios were set at 0.4, 0.5, and 0.6 and the sand rates were set at 30%, 35%, and 40% to investigate the effects of these factors on the oil absorption properties of the concrete, the variation of the oil absorption rate over time, and the compressive strengths at 28 days, 60 days, and 90 days. The compressive strength of oil absorbent concrete was improved by incorporating seashell powder (SC), alkali-modified seashell powder (SSC), and acid–base-modified seashell powder (CSC). The results showed that the optimal water–cement ratio for comprehensive oil absorption performance and compressive strength was 0.5, while the optimal sand ratio was 0.35. Compared with ordinary concrete, the oil absorption performance improved by 58.69%. The oil absorption rate decreased gradually over time. However, the oil absorption time could be effectively extended and the oil absorption performance could be improved by the addition of a silane modifier. The best method for seashell modification was acid–base modification. The compressive strength reached 14.32 Mpa at 28 days and 17.45 Mpa at 90 days, which was 19.62% higher than that of OAC. Scanning electron microscopy (SEM), mercury intrusion porosimetry (MIP), and X-ray diffraction (XRD) were used to analyze the microstructure of OAC. It was discovered that the inclusion of CSC caused a reaction with hydrocalumite in the concrete, resulting in the formation of alumohydrocalcite. Additionally, Ca(OH)2 in CSC facilitated the hydration reaction of mineral admixtures like fly ash and slag. At 28 days, more amorphous gels (C-S-H, C-(A)-S-H) and Aft were produced. The three components were combined to enhance the bonding between the cementitious materials and the aggregates, resulting in a denser internal structure of the OAC and improving its strength. This study promotes the use of OAC in slope protection projects.

Mechanical properties distribution of lime-fly ash solidified oil contaminated soil in a coastal environment

Effect of Stabilization/solidification on Mechanical and Phase Characteristics of Organic River Silt by a Stabilizer

Effects of salt and solidification treatment on the oil-contaminated soil: A case study in the coastal region of Tianjin, China

Incorporation of disposed oil-contaminated soil in cement-based materials

Experimental Study on Mechanical Properties of Soft Clay Stabilized by Industrial By-Products

Experimental Study on Mechanical Strength of Diesel-Contaminated Red Clay Solidified with Lime and Fly Ash

Study on the solidification of oily sludge

Engineering Properties of Heavy Metal Contaminated Soil Solidified/Stabilized with High Calcium Fly Ash and Soda Residue

Research on the Mechanism of Strength Improvement in Acid–Base-Activated Low Carbon Oil Absorbent Concrete

Comparison between reactive MgO- and Na2SO4-activated low-calcium fly ash-solidified soils dredged from East Lake, China

Study on properties and soil solidification mechanism of alkali - activated cementitious materials

Electrical resistivity of heavy metal contaminated soils solidified/stabilized with cement-fly ash

Utilization of Portland cement with limestone powder and cement kiln dust for stabilization/solidification of oil-contaminated marl soil

Mechanics, durability, and microstructure analysis of marine soil stabilized by an eco-friendly calcium carbide residue-activated coal gangue geopolymer

Preparation of non-sintered lightweight aggregates through co-mechanochemical treatment of oil-contaminated drill cuttings, circulation fluidized bed combustion fly ash, and quicklime

Mechanical Properties, Durability Performance, and Microstructure of CaO-Fly Ash Solidified Sludge from Northeast, China

Stabilization of iron ore tailing with low-carbon lime/carbide slag-activated ground granulated blast-furnace slag and coal fly ash

Experimental Study of the Working Property and Strength Behavior of Waste Marine Clay with High Water Content Modified with Quicklime, Ground Calcium Carbonate, and a WXS-II Soil Stabilizer

The Role of a New Stabilizer in Enhancing the Mechanical Performance of Construction Residue Soils

Stabilisation of oil-contaminated soils using microbially induced calcite crystals by bacterial flocs

Durability and Swelling of Solidified/Stabilized Dredged Marine Soils with Class-F Fly Ash, Cement, and Lime