Abstract:Composites that use fly ash and slag as alkali-activated materials instead of cement can overcome the defects and negative effects of alkali-activated cementitious materials prepared with the use of an alkali-activated material. In this study, fly ash and slag were used as raw materials to prepare alkali-activated composite cementitious materials. Experimental studies were carried out on the effects of the slag content, activator concentration and curing age on the compressive strength of the composite cementitious materials. The microstructure was characterized using hydration heat, X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), mercury intrusion porosimetry (MIP) and scanning electron microscopy (SEM), and its intrinsic influence mechanism was revealed. The results show that increasing the curing age improves the degree of polymerization reaction and the composite reaches 77~86% of its 7-day compressive strength after 3 days. Except for the composites with 10% and 30% slag content, which reach 33% and 64%, respectively, of their 28-day compressive strength at 7 days, the remaining composites reach more than 95%. This result indicates that the alkali-activated fly ash–slag composite cementitious material has a rapid hydration reaction in the early stage and a slow hydration reaction in the later stage. The amount of slag is the main influencing factor of the compressive strength of alkali-activated cementitious materials. The compressive strength shows a trend of continuous increase when increasing slag content from 10% to 90%, and the maximum compressive strength reaches 80.26 MPa. The increase in the slag content introduces more Ca2+ into the system, which increases the hydration reaction rate, promotes the formation of more hydration products, refines the pore size distribution of the structure, reduces the porosity, and forms a denser microstructure. Therefore, it improves the mechanical properties of the cementitious material. The compressive strength shows a trend of first increasing and then decreasing when the activator concentration increases from 0.20 to 0.40, and the maximum compressive strength is 61.68 MPa (obtained at 0.30). The increase in the activator concentration improves the alkaline environment of the solution, optimizes the level of the hydration reaction, promotes the formation of more hydration products, and makes the microstructure denser. However, an activator concentration that is too large or too small hinders the hydration reaction and affects the strength development of the cementitious material.

Study on properties and soil solidification mechanism of alkali - activated cementitious materials

Study on Mixing Cement-Waste By-Product to Stabilize Soft Marine Clay

Analysis of Strength Characteristics and Microstructure of Alkali-activated Slag Cement Fluidized Solidified Soil

Performance Optimization of Alkaline Multi-Industrial Waste-Based Cementitious Materials for Soil Solidification

Experimental Study on Mechanical Properties and Micro-Mechanism of All-Solid-Waste Alkali Activated Binders Solidified Marine Soft Soil

Experimental Study on Mechanical Properties of Soft Clay Stabilized by Industrial By-Products

Properties, Microstructure Development and Life Cycle Assessment of Alkali-Activated Materials Containing Steel Slag under Different Alkali Equivalents

Mechanical and durability properties of a soil stabilised with an alkali-activated cement

Strength formation mechanism and curing system optimization of low-carbon cementitious materials prepared by synergistic activation of multiple alkaline solid wastes

Microstructures and properties of alkali-activated slags with composite activator: Effects of Na2O equivalents

Study on the preparation, performance, and mechanism for solid waste cementitious materials

Study on the solidification property and mechanism of soft soil based on the industrial waste residue

Damage evolution, brittleness and solidification mechanism of cement soil and alkali-activated slag soil

Influence of Multiple Factors on the Workability and Early Strength Development of Alkali-Activated Fly Ash and Slag-Based Geopolymer-Stabilized Soil

Study on the Properties and Hydration Mechanism of Calcium Carbide Residue-Based Low-Carbon Cementitious Materials

Study of the Mechanical Properties and Microstructure of Alkali-Activated Fly Ash–Slag Composite Cementitious Materials

Study on the Property and Mechanism of Low Content Cement-Industrial Waste Residue Silt Solidification

Study on the Alkali–Sulfur Co-Activation and Mechanical Properties of Low-Carbon Cementitious Composite Materials Based on Electrolytic Manganese Residue, Carbide Slag, and Granulated Blast-Furnace Slag

Study on the Performance and Solidification Mechanism of Multi-Source Solid-Waste-Based Soft Soil Solidification Materials

Microstructure, strength development mechanism, and CO2 emission analyses of alkali-activated fly ash-slag mortars

Admixture Effects on the Rheological/Mechanical Behavior and Micro-Structure Evolution of Alkali-Activated Slag Backfills