Abstract:As a commonly reinforcing phase in wear-resistant materials, TiC is often added into wear-resistant materials to improve the wear resistance. The independently developed stepped molds with variable thicknesses were used to prepare the TiC-reinforced steels with the same composition though melt solidification processing to study the effect of the solidification rate on the particle size and wear performance. The effect of the hot rolling compression ratio on the particle size and wear performance was also studied. The length and aspect ratios of the particles in heat-treated TiC-reinforced steels with different billet thicknesses and rolling compression ratios were measured. With the increasing in the billet thickness and the decreasing in the rolling compression ratio, the length and aspect ratio of the particles increased in heat-treated TiC-reinforced steels, and the hardness decreased slightly. The three-body abrasive wear behavior of the TiC-reinforced steels was conducted using a standard dry sand rubber wheel wear testing procedure, and the modeling of the wear mechanism was established. The particle size is the main factor affecting wear resistance when the hardness of TiC-reinforced steels is similar. When the particles size is moderate, about 2–6 μm, the particle can break the sand tip and hinder the sand tip from sliding on the surface. In this manner, the mass loss decreased and the wear resistance improved. The large particles will be broken easily by the abrasive, and the small particles are removed easily by the abrasive in the wear process. So, the large and small particles cannot effectively prevent the damage of the abrasive to the matrix, and they have less of an effect on improving wear resistance.

Effects of TiC formation on the microstructure and hardness of wear-resistant steel

Effect of Solidification and Hot Rolling Processes on Wear Performance of TiC-Reinforced Wear-Resistant Steel

Microstructure, Mechanical Properties and Wear Resistance of Low Alloy Abrasion Resistant Martensitic Steel Reinforced with TiC Particles

Influence of Carbon Contents on the Structure and Tribocorrosion Properties of Tisicn Coatings on Ti6al4v

Effect of cooling rate on microstructure, hardness, and residual stress of 0.28C–0.22Ti wear-resistant steel

Superior wear resistance of dual-phased TiC–TiB2 ceramic nanoparticles reinforced carbon steels

Effect of Carbon Content on the Phase Composition, Microstructure and Mechanical Properties of the TiC Layer Formed in Hot-Pressed Titanium-Steel Composites

Effects of TiC and residual austenite synergistic strengthening mechanism on impact-abrasive wear behavior of bainite steel

Wear-Resistant TiC Strengthening CoCrNi-Based High-Entropy Alloy Composite

High-Titanium Steel: A Comprehensive Review of Research Progress

Interfacial bonding and wear behavior of macroscopic TiC particulates reinforced iron-based composites fabricated by infiltration casting process

Effect of Ce content on the microstructure and TiN precipitation behaviour of high-titanium steel during slow cooling solidification

Dry Sliding Wear Properties of Annealed Carbon Steels Matrix Composites by Nanosized TiC‐TiB2 Particles

Revealing the role of micron-sized in situ TiC particles on tensile properties and fracture mechanism of martensitic wear-resistant steel at elevated temperature

Effect of TiC on Microstructure and Properties of Wear-Resistant Mo2FeB2 Claddings

Effect of TiC on the impact abrasive wear resistance of low alloy martensitic steel

The effect of TiC on microstructure and mechanical properties of Ti-5553 beta phase titanium alloy

Effects of Ti3SiC2 on microstructure and properties of TiC0.4 enhanced TiAl matrix composites

Dry Sliding Wear Properties of Annealed Carbon Steels Matrix Composites by Nano‐Sized TiC‐TiB2 Particles

Tuning composition and microstructure by doping Ti and C for enhancing mechanical property and wear resistance of Al0.2Co1.5CrFeNi1.5Ti0.5 high entropy alloy matrix composites

High-temperature wear and cyclic oxidation behavior of (Ti, W)C reinforced stainless steel coating deposited by PTA on a plain carbon steel