Abstract:Composites that use fly ash and slag as alkali-activated materials instead of cement can overcome the defects and negative effects of alkali-activated cementitious materials prepared with the use of an alkali-activated material. In this study, fly ash and slag were used as raw materials to prepare alkali-activated composite cementitious materials. Experimental studies were carried out on the effects of the slag content, activator concentration and curing age on the compressive strength of the composite cementitious materials. The microstructure was characterized using hydration heat, X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), mercury intrusion porosimetry (MIP) and scanning electron microscopy (SEM), and its intrinsic influence mechanism was revealed. The results show that increasing the curing age improves the degree of polymerization reaction and the composite reaches 77~86% of its 7-day compressive strength after 3 days. Except for the composites with 10% and 30% slag content, which reach 33% and 64%, respectively, of their 28-day compressive strength at 7 days, the remaining composites reach more than 95%. This result indicates that the alkali-activated fly ash–slag composite cementitious material has a rapid hydration reaction in the early stage and a slow hydration reaction in the later stage. The amount of slag is the main influencing factor of the compressive strength of alkali-activated cementitious materials. The compressive strength shows a trend of continuous increase when increasing slag content from 10% to 90%, and the maximum compressive strength reaches 80.26 MPa. The increase in the slag content introduces more Ca2+ into the system, which increases the hydration reaction rate, promotes the formation of more hydration products, refines the pore size distribution of the structure, reduces the porosity, and forms a denser microstructure. Therefore, it improves the mechanical properties of the cementitious material. The compressive strength shows a trend of first increasing and then decreasing when the activator concentration increases from 0.20 to 0.40, and the maximum compressive strength is 61.68 MPa (obtained at 0.30). The increase in the activator concentration improves the alkaline environment of the solution, optimizes the level of the hydration reaction, promotes the formation of more hydration products, and makes the microstructure denser. However, an activator concentration that is too large or too small hinders the hydration reaction and affects the strength development of the cementitious material.

Microstructure and phase characterizations of fly ash cements by alkali activation

Strength and Microstructural Characteristics of Activated Fly Ash–Cement Paste

Effects of Na2CO3/Na2SiO3 Ratio and Curing Temperature on the Structure Formation of Alkali-Activated High-Carbon Biomass Fly Ash Pastes

Mechanical Properties of Fly Ash–Slag Based Alkali-Activated Materials under the Low-Energy Consummation-Sealed Curing Condition

Investigation of Low-Calcium Circulating Fluidized Bed Fly Ash on the Mechanical Strength and Microstructure of Cement-Based Material

Alkali-activated fly ash cured with pulsed microwave and thermal oven: A comparison of reaction products, microstructure and compressive strength

Performances and microstructure of one-part fly ash geopolymer activated by calcium carbide slag and sodium metasilicate powder

Strength characteristics of self-compacting concrete with alkali-activated fly ash

Formulation and characterization of cleaner one-part novel fly ash/lime-based alkali-activated material

Design and Microstructural Analysis of the Mixture Proportion of Alkali-Activated Fly Ash-Slag Composite Cementitious Material

Thermogravimetric analysis and phase characterizations of Portland fly ash limestone cements

Effect of Ordinary Portland Cement and Water Glass on the Properties of Alkali Activated Fly Ash Concrete

Study of the Mechanical Properties and Microstructure of Alkali-Activated Fly Ash–Slag Composite Cementitious Materials

Comparative mechanical and microstructural properties of high calcium fly ash one-part geopolymers activated with Na2SiO3-anhydrous and NaAlO2

Early activation of high volume fly ash by ternary activator and its activation mechanism

Characterization of Fly Ash Alkali Activated Foams Obtained Using Sodium Perborate Monohydrate as a Foaming Agent at Room and Elevated Temperatures

Effects of Fly Ash Inclusion and Alkali Activation on Physical, Mechanical, and Chemical Properties of Clay

Influence of Activators on Mechanical Properties of Modified Fly Ash Based Geopolymer Mortars

Mechanical Properties of High Early Strength Class C Fly Ash-Based Alkali Activated Concrete

Influence of alkaline activator solution ratio on the properties of biomass fly ash-based alkali-activated materials

Effect of fly ash on the atomic scale structure of C–S–H during Portland Cement hydration