Ultrastable All-Solid-State Sodium Rechargeable Batteries
Jing Yang,Gaozhan Liu,Maxim Avdeev,Hongli Wan,Fudong Han,Lin Shen,Zheyi Zou,Siqi Shi,Yong-Sheng Hu,Chunsheng Wang,Xiayin Yao
DOI: https://doi.org/10.1021/acsenergylett.0c01432
IF: 22
2020-08-11
ACS Energy Letters
Abstract:The insufficient ionic conductivity of oxide-based solid electrolytes and the large interfacial resistance between the cathode material and the solid electrolyte severely limit the performance of room-temperature all-solid-state sodium rechargeable batteries. A NASICON solid electrolyte Na<sub>3.4</sub>Zr<sub>1.9</sub>Zn<sub>0.1</sub>Si<sub>2.2</sub>P<sub>0.8</sub>O<sub>12</sub>, with superior room-temperature conductivity of 5.27 × 10<sup>–3</sup> S cm<sup>–1</sup>, is achieved by simultaneous substitution of Zr<sup>4+</sup> by aliovalent Zn<sup>2+</sup> and P<sup>5+</sup> by Si<sup>4+</sup> in Na<sub>3</sub>Zr<sub>2</sub>Si<sub>2</sub>PO<sub>12</sub>. The bulk conductivity and grain boundary conductivity of Na<sub>3.4</sub>Zr<sub>1.9</sub>Zn<sub>0.1</sub>Si<sub>2.2</sub>P<sub>0.8</sub>O<sub>12</sub> are nearly 20 times and almost 50 times greater than those of pristine Na<sub>3</sub>Zr<sub>2</sub>Si<sub>2</sub>PO<sub>12</sub>, respectively. The FeS<sub>2</sub>||polydopamine-Na<sub>3.4</sub>Zr<sub>1.9</sub>Zn<sub>0.1</sub>Si<sub>2.2</sub>P<sub>0.8</sub>O<sub>12</sub>||Na all-solid-state sodium batteries, with a polydopamine modification thin layer between the solid electrolyte and the cathode, maintain a high reversible capacity of 236.5 mAh g<sup>–1</sup> at a 0.1 C rate for 100 cycles and a capacity of 133.1 mAh g<sup>–1</sup> at 0.5 C for 300 cycles, demonstrating high performance for all-solid-state sodium batteries.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsenergylett.0c01432?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsenergylett.0c01432</a>.Experimental section; XRD, NPD, SEM, and EIS measurements for different solid electrolyte materials; STEM-EDS and DC polarization measurement for Zn0.1 sample; EDS measurement for Zn0.1 sample before and after contact with sodium; unit cell parameters of different solid electrolyte materials; structural parameters of different solid electrolyte materials; BVEL analysis and the comparison of bottleneck sizes; conductivities, activation energies, and relative densities of different solid electrolyte materials; FTIR measurement for Zn0.1 pellet with and without PDA layer; charge–discharge curves of FeS<sub>2</sub>||Zn0.1||Na all-solid-state battery; comparison of conductivities and battery performances reported in the literature and in this work; cross-sectional images of the cathode/electrolyte interface before and after cycling (<a class="ext-link" href="/doi/suppl/10.1021/acsenergylett.0c01432/suppl_file/nz0c01432_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology,energy & fuels,electrochemistry