Abstract:This study investigated the microstructure, residual stress, and fatigue behavior of duplex stainless steels that have been annealed with different annealing processes. A cold-rolled AISI 2205 Duplex Stainless Steel (DSS) sample was annealed in three ways for this purpose. In modes 1 and 2, samples were annealed at 500°C for 6 and 8 hours, respectively. The sample was annealed for 6 hours at 950°C for mode 3.The Optical Microscopy (OM) technique was used to determine the crystallographic texture and microstructural characteristics. An X-ray Diffraction (XRD) analysis was used to determine the residual stresses in austenite and ferrite phases on pre- and post-heat-treated samples. The Scanning Electron Microscope (SEM) technique was utilized to assess fatigue cracks. The results showed that the texture microstructure of the specimens using mode 1 and 2 were remained; the grain had a smaller fragmentation. The elongation grains of the specimen after mode 3 were smaller, relatively spheroidal, and more homogeneous. There was a reduction in residual stress after mode 3 annealing process. The fatigue strength of the specimens that under applied this process was 11.1% higher than that of specimens in the as-received state. On examine encore le traitement thermique pour améliorer les propriétés mécaniques de l'acier, puisque c'est un procédé complexe qui a besoin d'être étudié en profondeur. Dans l'étude en cours, on a réalisé une étude de la microstructure, des contraintes résiduelles et du comportement à la fatigue des aciers inoxydables duplex qui one été recuits avec différents traitements de recuit. Dans cette étude, on a recuit de trois façons des échantillons laminés à froid d'acier inoxydable duplex (DSS) AISI 2205. Dans les modes 1 et 2, on a recuit les échantillons à 500°C pendant 6 et 8 heures, respectivement. Pour le mode 3, on a recuit les échantillons pendant 6 heures à 950°C. La technique de microscopie optique (MO) a déterminé la texture cristallographique et les caractéristiques microstructurales. On a utilisé une analyse de diffraction des rayons X (XRD) pour déterminer les contraintes résiduelles dans les phases d'austénite et de ferrite des échantillons pré- et post-traités thermiquement. La technique du microscope électronique à balayage (MEB) a évalué les fissures de fatigue. Les résultats ont montré que la texture de la microstructure des spécimens utilisant les modes 1 et 2 demeurait en place; le grain présentait une plus petite fragmentation. Les grains allongés des spécimens après le mode 3 étaient plus petits, relativement sphériques et plus homogènes. Il y avait une réduction de la contrainte résiduelle après le procédé de recuit du mode 3. La résistance à la fatigue des spécimens qui ont subi ce procédé était de 11.1% supérieure à celle des spécimens à l'état tel que reçu.

Improving the Mechanical Properties of AISI 2205 Duplex Stainless Steel by Cryogenic Treatment Process

Enhanced mechanical and anticorrosion properties in cryogenic friction stir processed duplex stainless steel

Effect of annealing process on microstructure, residual stress, and fatigue behaviour of AISI 2205 duplex stainless steel

Influence of Cryogenic Treatments on the Wear Behavior of AISI 420 Martensitic Stainless Steel

Effect of Warm Rolling and Annealing on Microstructure, Texture, and Mechanical Properties of a 2205 Duplex Stainless Steel

Effect of Cryogenic Treatment on the Mechanical Properties of Alloy Steel 16MnCr5

Improved Surface Morphology and Corrosion Resistance Performance of 2205 Duplex Stainless Steel by Low Temperature Gas Nitriding

The Strengthening Role of Cryogenic Treatment in the Mechanical Properties and Abrasive Wear of Low Alloy Wear-Resistant Steel

Assessment of Properties on AISI430 Ferritic Stainless Steel by Nitriding process

Experimental Investigation on the Effect of Deep Cryogenic Treatment on 100 Cr6 Bearing Steel

AISI 2205 DSS for body-in-white automotive structure: effect of welding current and time on the performance of spot welded joint

Enhancing the Wear Resistance of 100Cr6 Bearing Steel Using Cryogenic Treatment

Investigating the wear resistance of AISI 410/AISI 2205 hybrid weld cladding on annealed EN 8 medium carbon steel

Optimization of cryogenic treatment to maximize the wear resistance of 18% Cr martensitic stainless steel by Taguchi method

A Novel Duplex Treatment of C20 Steel Combining Low-Pressure Carburizing and Laser Quenching

Effect of Deep Cryogenic Treatment on Corrosion Behavior of AISI H13 Die Steel

Deep Cryogenic Treatment Improves Wear Resistance of En 31 Steel

Effect of cryogenic treatment on tensile behavior of case carburized steel-815M17

Effect of Aqueous Soluted Nitriding Process on AISI 304 Austenitic Stainless Steel under Dry Sliding Conditions

Effect of Thermal Cycles on the Corrosion and Mechanical Properties of UNS S31803 Duplex Stainless Steel