Effect of Warm Rolling and Annealing on Microstructure, Texture, and Mechanical Properties of a 2205 Duplex Stainless Steel

Tairine Berbert Tavares,Daniella Gomes Rodrigues,Dagoberto Brandão Santos

DOI: https://doi.org/10.1002/srin.201900543

IF: 2.1258

2020-04-01

steel research international

Abstract:<p>The effect of warm rolling and annealing processes on the microstructure, microtexture, and mechanical properties of a 2205 duplex stainless steel was investigated in the present work. To evaluate the microstructure, scanning and transmission electron microscopy, and electron backscatter diffraction were used as main techniques. The mechanical properties were assessed through tensile tests. A transition from a bamboo type into a pearl structure was observed as the thickness reduction increased. Furthermore, the ferrite phase presented a weakening of α‐fiber, (&lt;011&gt;//RD), and a development of γ‐fiber, (&lt;111&gt;//ND), while the austenite had a reduction in the intensity of {110}&lt;112&gt; Brass component and a strengthening of {110}&lt;001&gt; Goss and {112}&lt;111&gt; Copper components. Multi‐stage work hardening behavior was observed by Jaoul‐Crussard analysis, which indicated the presence of secondary deformation mechanisms during the plastic deformation of the steel. Post deformation SEM and TEM results revealed the formation of α' and ε‐martensite at deformed regions. The orientation relationship developed between γ and ε‐martensite was Shoji‐Nishiyama (S‐N) &lt;110&gt;_γ//&lt;2110&gt;_ε.</p><p>This article is protected by copyright. All rights reserved.</p>

metallurgy & metallurgical engineering