Abstract:Ammonia is a well-known additive to promote crystal growth in hydrothermal synthesis of ZnO nanowires. Although the effect of ammonia on the nanowire growth has been intensively investigated, its influence on the seed layer, which governs the initial nanowire growth, is rarely discussed. Here, we demonstrate that ammonia strongly affects the seed layer as well as the following nanowire growth. On increasing the ammonia concentration, the nanowire density first increases and then decreases, while the nanowire growth rate keeps increasing. Experimental results and thermodynamic calculations of the initial growth process reveal that the transformation of the seed layer induced by ammonia prior to nucleation critically determines the nanowire density and thus also influences the following nanowire growth. Present results highlight the critical importance of discussing the variation of seed layers in ammonia-involved hydrothermal synthesis and suggest a novel seed engineering approach for tailoring the ZnO nanowire growth.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.jpcc.0c05490?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.jpcc.0c05490</a>.SEM images, diameter and areal density of ZnO nanowires grown with various seed layer thicknesses. The data was taken with a growth time of 3 h and without NH<sub>3</sub> (Figure S1); pH value and temperature of growth solution over time (Figure S2); EDS mapping analysis of the seed layer on a silicon substrate after immersing into growth solution with varying ammonia concentration for 10 and 30 min, respectively (Figure S3); thermodynamic calculation of Zn(II) solubility in aqueous solutions (S4); speciation of dissolved Zn(II) versus pH and temperature in growth solution (Figure S5) (<a class="ext-link" href="/doi/suppl/10.1021/acs.jpcc.0c05490/suppl_file/jp0c05490_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Ammonia-Induced Seed Layer Transformations in a Hydrothermal Growth Process of Zinc Oxide Nanowires

Effect of ammonia on morphology, wettability and photoresponse of ZnO nanorods grown by hydrothermal method

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Improved seedless hydrothermal synthesis of dense and ultralong ZnO nanowires.

Alignment-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

Controlling the hydrothermal growth and the properties of ZnO nanorod arrays by pre-treating the seed layer

Sequential Occurrence of ZnO Nanopaticles, Nanorods, and Nanotips During Hydrothermal Process in a Dilute Aqueous Solution

Facile and Controllable Growth of ZnO 1D Nanostructure Arrays on Zn Substrate by Hydrothermal Process

The effect of pre-annealing of sputtered ZnO seed layers on growth of ZnO nanorods through a hydrothermal method

Effect of Growth Time and Annealing on the Structural Defect Concentration of Hydrothermally Grown Zno Nanowires

Structure Transformation of Hydrothermally Treated ZnO Nanorod Array

Growth And Characterization Of Cu-Catalyzed Zno Nanowires

The influence of aqueous ammonia on nano-ZnO

Ultrathin Seed-Layer for Tuning Density of ZnO Nanowire Arrays and Their Field Emission Characteristics

Controllable Hydrothermal Synthesis of ZnO Nanowires Arrays on Al-doped ZnO Seed Layer and Patterning of ZnO Nanowires Arrays Via Surface Modification of Substrate

Effect of annealing of ZnO/Ag double seed layer on the electrical properties of ZnO/Ag/ZnO heterostructure nanorods

Growth and comparison of different morphologic ZnO nanorod arrays by a simple aqueous solution route

The Effect of the Texture and the Density of ZnO Seed Layer on the Orientation of ZnO Nanorod Arrays.

Effect of Seed Layer on the Growth of Zinc Oxide Nanowires by Chemical Bath Deposition Method

Hydrothermal Grow th of Vertical and Uniform ZnO Nanorod Arrays and Related Influences

Growth of flower-like ZnO on ZnO nanorod arrays created on zinc substrate through low-temperature hydrothermal synthesis