Microstructure, Mechanical Properties and Fracture of EP-823 Ferritic/Martensitic Steel After High-Temperature Thermomechanical Treatment

K. V. Almaeva,I. Yu. Litovchenko,N. A. Polekhina

DOI: https://doi.org/10.1007/s11182-020-02101-8

2020-09-01

Russian Physics Journal

Abstract:The paper investigates the microstructure and mechanical properties of the EP-823 ferritic/martensitic steel containing 12 wt.% chromium after the high-temperature thermomechanical treatment with plastic deformation in the austenite region, at a temperature ranging from –70 to –40°С, 20°С and from 650 to 720°С. The high-temperature thermomechanical mode results in the formation of the hetero-phase microstructure with high dispersible nanoparticles of the МХ type (V, Nb, Mo) and (C, N) and the higher dislocation density. The mechanical properties of steel obtained in this mode are higher than that obtained in the mode of conventional thermal treatment in the indicated temperature range. At low temperatures from –70 to –40°С, the yield stress increases by approximately 100–200 MPa, whereas at higher temperatures from 650 to 720°С, it changes only by 14 MPa. At low temperatures, the steel fracture elongation varies between 12.7–14.3% in using the high-temperature thermomechanical mode. The steel fracture occurs with the neck formation. At high temperatures, a plastic cup fracture occurs, and at room temperature brittle failure and microcracks are observed along with the plastic cup fracture. The brittle fracture considerably increases at low temperatures, the size and the number of microcracks also grow.

physics, multidisciplinary