Effect of high-temperature thermomechanical treatment on microstructure and mechanical properties of an austenitic steel with dispersed particles

S. A. Akkuzin,I. Yu. Litovchenko,A. N. Tyumentsev
DOI: https://doi.org/10.1063/5.0034420
2020-01-01
Abstract:The features of microstructure and mechanical properties of an austenitic reactor steel with dispersed particles after high-temperature thermomechanical treatment with plastic deformation after heating to <i>T</i> = 1100 and 600°C are investigated. It is shown that as a result of processing with heating to <i>T</i> = 1100°C, plastic deformation develops in localized regions of the material and a fragmented microstructure with predominantly low-angle misorientation boundaries is formed. After deformation with heating to <i>T</i> = 600°C, fragmentation develops more intensively with the formation of both low- and high-angle misorientation boundaries. The elemental composition of dispersed carbide particles of the MC type in steel is studied. It is shown that these particles have a complex composition based on Ti, Nb, and Mo. The elemental composition of the matrix after the treatments corresponds to the nominal one, which indicates that a significant proportion of carbide-forming elements remains in the solid solution and does not participate in the formation of dispersed particles. These structural states provide an increase in the yield strength of steel up to ≈550– 740 MPa compared to the initial values with a relative elongation of ≈7–12.5%. It should be noted that the main contribution to strengthening (Δσ ≈ 350–540 MPa) is provided by the fragmented structure, while the contribution of dispersed particle hardening is Δσ<sub>disp</sub>≤35 MPa.
What problem does this paper attempt to address?