Effect of heat treatment on microstructure and mechanical properties of S31042 austenite heat resistant steel

YANG Zheng,ZHAO Xin-bao,ZHANG Xing-xing,DANG Ying-ying,LU Jin-tao,YUAN Yong

DOI: https://doi.org/10.13289/j.issn.1009-6264.2017-0431

2018-01-01

Abstract:Microstructure and mechanical properties of S31042 austenite heat resistant steel after different heat treatments were studied by means of scanning electron microscopy (SEM),energy dispersive spectrometer (EDS) analysis and MTS universal testing machine.The results show that with the increasing of aging temperature from 700 ℃ to 900 ℃,the precipitation amount of M23 C6 carbides at grain boundaries increases,and gradually exhibits a continuous distribution,and the impact toughness of the steel decreases significantly,the tensile strength at high temperature of the steel decreases gradually,and the yield strength approximately remains stable,but the yield strength increases slightly after aging at 900 ℃ for 1 h.However,when the aging temperature increasing from 900 ℃ to 1000 ℃,the precipitation amount of the M23 C6 carbides at grain boundaries decreases,the tensile strength at high temperature of the steel changes little,the yield strength decreases,and the impact toughness increases.Compared with the low strain rate in the tensile process,the aggregation precipitation of the M23 C6 phases at grain boundary leads to an increase in the tendency of intergranular cracking under the condition of high instantaneous impact and high strain rate.