Abstract:A comparative investigation of two fundamentally different approaches for the synthesis, microstructure evolution, and mechanical properties of the refractory‐high‐entropy alloys (RHEA) HfNbTaTiZr and HfNbTiZr was performed. The two methods comprised conventional arc (button) melting, and a powder route based on mechanical alloying and consolidation via severe plastic deformation (SPD). Powder consolidation via SPD involved different ranges of hydrostatic pressure, strain, and temperature. In particular, blended elemental (BE) powder was pre‐compacted and subjected to one or four passes of equal channel angular pressing (ECAP) at 500°C and then ten revolutions of high‐pressure torsion (HPT) at room temperature to an effective strain between 4 and 40. Some samples were then annealed at 500°C for one hour to investigate the thermal stability of the phases. The four ECAP passes at 500oC did not result in the formation of the BCC phase typical for the program RHEAs despite the presence of interfacial zones between particles and defect‐driven diffusion. Nevertheless, a single ECAP pass was sufficient to create a solid bulk sample for subsequent HPT. After ten HPT revolutions, in contrast to melting route resulting in a predominantly, as confirmed by majority of published research, single BCC phase alloy, both alloys formed new phases comprising on average 82% of a Nb‐rich BCC phase and ∽18% of a ZrHf‐rich HCP phase in M1 alloy, and 85% a Nb‐rich BCC phase and ∽15% of a ZrHf‐rich HCP phase in M2 alloy. After annealing treatment, the volume fraction of BCC phase decreased on average to 75% and volume fraction of HCP phase increased to ∽25% in both alloys. Notably as result of annealing, the BCC phase in M2 alloy was transformed into two BCC phases with different cell parameters. That results in significantly increased hardness by (Hv 150‐200). This article is protected by copyright. All rights reserved.

Preparation of Refractory High-Entropy Alloys by Electro-Deoxidation and the Effect of Heat Treatment on Microstructure and Hardness

High Temperature Oxidation Behavior of TiNbMoAlSi Refractory High Entropy Alloy Developed by Electron Beam Additive Manufacturing

Development of Oxidation Resistant Refractory High Entropy Alloys for High Temperature Applications: Recent Results and Development Strategy

Composition control and heat treatment effect on characteristics of ZrNbTaHf x refractory high entropy alloys

Oxidation Behavior Between 700 And 1300 Degrees C Of Refractory Tizrnbhfta High-Entropy Alloys Containing Aluminum

Microstructure and Mechanical Properties of Alx(TiZrTa0.7NbMo) Refractory High-Entropy Alloys

Controlling microstructure and mechanical properties of Ti-V-Cr-Nb-Ta refractory high entropy alloys through heat treatments

Refractory high-entropy nanoalloys with exceptional high-temperature stability and enhanced sinterability

Refractory High‐Entropy Alloys Produced from Elemental Powders by Severe Plastic Deformation

Enhanced High-Temperature Strength of HfNbTaTiZrV Refractory High-Entropy Alloys by AI 2O 3 Reinforcement

Microstructure and Mechanical Properties of the Ductile Al–Ti–Mo–Nb–V Refractory High Entropy Alloys

Uniting superior mechanical properties with oxidation resistance in a refractory high-entropy alloy via Cr and Al alloying

Preparation of CoCrFeNi High-Entropy Alloy via Electro-Deoxidation of Metal Oxides

Microstructure and mechanical properties of the TiZrNbMoTa refractory high-entropy alloy produced by mechanical alloying and spark plasma sintering

Oxidation Behavior between 700 and 1300 °C of Refractory TiZrNbHfTa High-Entropy Alloys Containing Aluminum

Microstructure and Mechanical Properties of a New Refractory HfNbSi<sub>0.5</sub>TiVZr High Entropy Alloy

Oxidation behavior of the Ti38V15Nb23Hf24 refractory high-entropy alloy at elevated temperatures

Oxidation resistance of Al-containing refractory high-entropy alloys

Study on mechanical alloying behavior and thermal stability of HfMoNbTaTi refractory high-entropy alloy

Microstructure and tribological properties of TiZrV0.5Nb0.5Al refractory high entropy alloys at elevated temperature

Superior Oxidation Resistance of a Y-Hf Co-Doped Al18Co30Cr10Fe10Ni32 Eutectic High-Entropy Alloy at 1100-1300 °C