Abstract:Air-cooling from an intercritical (IC) temperature produced an acicular pearlite in ferrite structure and was effective in increasing the strength and ductility of ductile iron in sections up to 10 inches (250 mm). Five alloys were melted and poured as 3-inch Y-blocks, and IC heat treatment produced a fine-grained acicular pearlite + ferrite structure in all five alloys. The compositions ranged from 3.39–3.59% C, 2.34–2.45% Si, 0.29–0.44% Mn, 0.59–0.61% Cu and 0.24–1.78 % Ni, with CE ranging from 4.34 to 4.40. Samples were removed from the bottoms of the Y-blocks to obtain test samples for tensile and Charpy V-Notch (CVN) impact testing. The test samples were heat-treated at intercritical temperatures near the upper critical temperature (UCT) and cooled at various rates to simulate air-cooling of castings up to 10 inches (250 mm). Prior to intercritical heat treatment, experiments were conducted to determine the optimum heat treatment parameters. It was found that the path of the thermal cycle on heating to the IC temperature can affect the quality of the heat-treated structure. Among the things learned are the following: The lamellar austenite in ferrite structure persisted at temperatures as high as 60° F above the predicted UCT. Heat treatment at UCT + 20 °F produced the most dense, acicular pearlite + ferrite structure. Ferritizing prior to IC heat treatment minimizes the pearlite network in the cell boundaries. A minimum soak time of 2 h at the IC temperature is recommended. The lamellar structure is stable for at least 8 h. Copper appears to delay the time to reach equilibrium at the UCT. Nickel (at 1.8%) counteracts the Cu effect. The IC heat-treated samples displayed significantly higher ferrite contents over the as-cast materials. The high strength and elongation were attributed to grain refinement and increased ferrite contents, respectively. Furthermore, the material appears to be forgiving of marginal graphite structures. Despite the coarse graphite inclusions with poor shapes, 7–9% elongation was attained in test bars exceeding 60 ksi (414 MPa) yield strength when cooled as a 10-inch (250 mm) section.

Improving High-Temperature Performance of High Si-Alloyed Ductile Iron by Altering Additions

Control of High-Temperature Static and Transient Thermomechanical Behavior of SiMo Ductile Iron by Al Alloying

Improvement of High-Temperature Performance of High Si SGI by Al Alloying and Optimizing Microstructural Dispersity

Development of New Ductile Iron with Super-High Thermal Conductivity and Elongation

Effects of Cu Addition on the Microstructure and Properties of the Al–Mn–Fe–Si Alloy

Effect of Silicon and Graphite Degeneration on High-Temperature Oxidation of Ductile Cast Irons in Open Air

Effect of Micro-Structural Dispersity of SiMo Ductile Iron on High Temperature Performance during Static Oxidation

Effect of Molybdenum Contents on Microstructure and High-Temperature Wear Behavior of SiMo Ductile Iron

Influence of Cooling Rate and Alloying by "Cr, V, and Ni" on Microstructure and High-Temperature Wear Behavior of SiMo Ductile Iron

Modification of Silicon Microsegregation in Solid-Solution-Strengthened Ductile Iron by Alloying with Aluminum

Evolution of Iron-Rich Intermetallics and its Effect on the Mechanical Properties of Al-Cu-Mn-Fe-Si Alloys after Thermal Exposure and High-Temperature Tensile Testing

High temperature oxidation of inoculated high Si/SiMo ductile cast irons in air and combustion atmospheres

Tempering temperature dependence on the microstructure, mechanical properties and wear behaviour of a novel high chromium cast iron

Achieving Higher Strength and Ductility in Heavy-Section Ductile Iron Castings

Effect of Iron-Rich Intermetallic and Eutectic Si Accumulation on Al-Si-Mg Alloy

Evaluation of Microstructure and Abrasive Wear-Resistance of Medium Alloy SiMo Ductile Cast Iron

The effect of chromium additions on the mechanical properties of Ni-25Al-27.5Fe-based intermetallic compounds

Effect of Silicon Micro-Alloying on the Thermal Conductivity, Mechanical Properties and Rheological Properties of the Al–5Ni Cast Alloy

Effects of Manganese and Heat Treatment on Mechanical Properties in Spheroidal Graphite Cast Iron

Microstructure and Mechanical Properties of Cast Al-Li-Mg Alloy: Role of Cu Addition and Heat Treatment

Effect of Mg Content on the Shear Strength of Al-Si-Mg and Al-Si-Cu Alloys at Elevated Temperatures